Fujipoly Industries Sarcon® 45U Thin-Film UR

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® 45U Thin-Film UR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon UR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 79
79
ASTM D2240
88
88
60°C for 500 hrs with 95% RH; ASTM D2240
91
91
150°C for 1,000 hrs; ASTM D2240
93
93
200°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 2.66 MPa
386 psi
3.77 MPa
547 psi
60°C for 500 hrs with 95% RH
4.22 MPa
612 psi
150°C for 1,000 hrs
6.66 MPa
966 psi
200°C for 1,000 hrs
Elongation at Yield 47 %
47 %
200°C for 1,000 hrs
50 %
50 %
150°C for 1,000 hrs
83 %
83 %
60°C for 500 hrs with 95% RH
110 %
110 %
Tear Strength 0.400 kN/m
2.28 pli
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 6.10e+13 ohm-cm
6.10e+13 ohm-cm
60°C for 500 hrs with 95% RH
1.00e+15 ohm-cm
1.00e+15 ohm-cm
2.00e+15 ohm-cm
2.00e+15 ohm-cm
200°C for 1,000 hrs
1.00e+16 ohm-cm
1.00e+16 ohm-cm
150°C for 1,000 hrs
Dielectric Constant 4.42

@Frequency 1000 Hz
4.42

@Frequency 1000 Hz
After 1000 hrs at 200°C
4.43

@Frequency 50 Hz
4.43

@Frequency 50 Hz
After 1000 hrs at 200°C
4.44

@Frequency 1e+6 Hz
4.44

@Frequency 1e+6 Hz
After 1000 hrs at 200°C
4.52

@Frequency 1000 Hz
4.52

@Frequency 1000 Hz
After 1000 hrs at 150°C
4.53

@Frequency 50 Hz
4.53

@Frequency 50 Hz
After 1000 hrs at 150°C
4.54

@Frequency 1e+6 Hz
4.54

@Frequency 1e+6 Hz
After 1000 hrs at 150°C
4.63

@Frequency 1000 Hz
4.63

@Frequency 1000 Hz
4.64

@Frequency 1e+6 Hz
4.64

@Frequency 1e+6 Hz
4.64

@Frequency 50 Hz
4.64

@Frequency 50 Hz
4.65

@Frequency 1e+6 Hz
4.65

@Frequency 1e+6 Hz
After 500 hrs at 60°C with 95% RH
4.71

@Frequency 1000 Hz
4.71

@Frequency 1000 Hz
After 500 hrs at 60°C with 95% RH
4.79

@Frequency 50 Hz
4.79

@Frequency 50 Hz
After 500 hrs at 60°C with 95% RH
Dielectric Strength 12.0 kV/mm
305 kV/in
AC 60 Hz
13.0 kV/mm
330 kV/in
150°C for 1,000 hrs
13.0 kV/mm
330 kV/in
200°C for 1,000 hrs
13.0 kV/mm
330 kV/in
60°C for 500 hrs with 95% RH
Dielectric Breakdown 8000 V
8000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.00060

@Frequency 1e+6 Hz
0.00060

@Frequency 1e+6 Hz
After 1000 hrs at 200°C
0.00070

@Frequency 50 Hz
0.00070

@Frequency 50 Hz
After 1000 hrs at 150°C
0.00070

@Frequency 1000 Hz
0.00070

@Frequency 1000 Hz
After 1000 hrs at 150°C
0.00070

@Frequency 1e+6 Hz
0.00070

@Frequency 1e+6 Hz
After 1000 hrs at 150°C
0.00080

@Frequency 1000 Hz
0.00080

@Frequency 1000 Hz
After 1000 hrs at 200°C
0.00090

@Frequency 1e+6 Hz
0.00090

@Frequency 1e+6 Hz
0.0013

@Frequency 1000 Hz
0.0013

@Frequency 1000 Hz
0.0013

@Frequency 50 Hz
0.0013

@Frequency 50 Hz
After 1000 hrs at 200°C
0.0024

@Frequency 50 Hz
0.0024

@Frequency 50 Hz
0.0035

@Frequency 1e+6 Hz
0.0035

@Frequency 1e+6 Hz
After 500 hrs at 60°C with 95% RH
0.0069

@Frequency 1000 Hz
0.0069

@Frequency 1000 Hz
After 500 hrs at 60°C with 95% RH
0.0186

@Frequency 50 Hz
0.0186

@Frequency 50 Hz
After 500 hrs at 60°C with 95% RH
Descriptive Properties Value Comments
Color Grey
Thermal Impedance 0.35°C/W
FTM P-3010; ASTM D5470