Glastic SG-200 Industrial Lift Magnet
| Category | Polymer , Thermoset , Composite SMC , Filled/Reinforced Thermoset , Polyester, TS |
| Manufacturer | Glastic |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Glastic SG-200 Industrial Lift Magnet.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glastic Grade SG-200 high-strength and high-temperature laminates offer temperature ratings of up to 210°C. SG-200 is ideal for a wide variety of product applications requiring high-temperature NEMA GPO-1 products. It is also a superior replacement material for epoxy-bonded mica in layer insulation applications. SG-200 features the following: Extremely strongExcellent retention of properties at elevated temperaturesIdeal for high temperature applicationsEasily fabricatedAsbestos-FreeInformation provided by Glastic Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D-792 |
| Water Absorption | 0.30 % | 0.30 % | % by wt.; ASTM D-570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D-638 |
| Tensile Modulus | 11.7 GPa | 1700 ksi | ASTM D-638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D-790 |
| Compressive Strength | 248 MPa | 36000 psi | ASTM D-695 |
| Shear Strength | 76.5 MPa | 11100 psi | ASTM D-732 |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | ASTM D-256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
ASTM D-696 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | ASTM C-177 |
| UL RTI, Electrical | 210 °C | 410 °F | UL 746B |
| UL RTI, Mechanical without Impact | 210 °C | 410 °F | UL 746B |
| Flammability, UL94 | HB | HB | |
| Oxygen Index | 21.8 % | 21.8 % | ASTM D-2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | 1.45e+14 ohm | 1.45e+14 ohm | ASTM D-257 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
ASTM D-150 |
| 4.6 @Frequency 60 Hz |
4.6 @Frequency 60 Hz |
ASTM D-150 | |
| Dielectric Strength | 19.6 kV/mm | 498 kV/in | Perpendicular S/T in Air; ASTM D-149 |
| 24.6 kV/mm | 625 kV/in | Perpendicular S/T in Oil; ASTM D-149 | |
| Dissipation Factor | 0.013 @Frequency 1e+6 Hz |
0.013 @Frequency 1e+6 Hz |
ASTM D-150 |
| 0.037 @Frequency 60 Hz |
0.037 @Frequency 60 Hz |
ASTM D-150 | |
| Arc Resistance | 120 sec | 120 sec | ASTM D-495 |
| 180 sec | 180 sec | Post-cured; ASTM D-495 | |
| Comparative Tracking Index | >= 500 V | >= 500 V | UL 746A |
| Hot Wire Ignition, HWI | 35 sec @Thickness 0.711 mm |
35 sec @Thickness 0.0280 in |
UL 746A |
| 39 sec @Thickness 1.47 mm |
39 sec @Thickness 0.0580 in |
UL 746A | |
| High Amp Arc Ignition, HAI | >= 200 arcs | >= 200 arcs | #Exposure; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 mm/min | 0.000 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Electric Strength kV, ASTM D149 | 50 | Parallel S/S in Oil |
| Standard Color | Natural/Tan | |
| UL Recognition File Number | E81928 |