Global HI-830 High Impact Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Global Polymers Corporation |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Global HI-830 High Impact Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flowGood stiffnessApplications:AppliancesElectrical/Electronic applicationsHousehold goodsFood packagingToys
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 71 @Thickness 6.35 mm |
71 @Thickness 0.250 in |
ASTM D785 |
| Tensile Strength, Yield | 21.4 MPa | 3100 psi | ASTM D638 |
| Flexural Yield Strength | 41.4 MPa | 6000 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 1.57 J/cm @Thickness 6.35 mm, Temperature 22.8 °C |
2.94 ft-lb/in @Thickness 0.250 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 6.35 mm |
194 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 96.1 °C | 205 °F | ASTM D1525 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Transparent | |
| Forms | Pellets |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 4002 C BLK 40% Filler Content Polypropylene
- Plastcom SLOVAMID 66 GF 14 HI TS PA66, 14% glass fibre, improved strength
- Polyplastic Torlen® PE 2K 901 High Density Polyethylene, Carbon Filled
- Parker Chomerics CHO-BOND 320 Pressure Sensitive Adhesive
- SABIC Innovative Plastics LNP Faradex MS002P PP (Asia Pacific)
- Saint-Gobain CHR® 2300-5R UHMW Film Backing Natural Rubber Adhesive Pressure Sensitive Tape
- Wellman Wellamid® MRGST1715-WBK1 Nylon 6, 25% Mineral and Glass Sphere Reinforced, Impact Modified, Weatherable Grade
- ExxonMobil LLDPE LL 1002YB Wire & Cable Linear Low Density Polyethylene Resin
- DuPont Teijin Films Melinex® S Polyester Film, 75 Gauge
- Asahi Kasei Thermylene® P6-30FG-0699 30% Glass Fiber Reinforced, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved