Gromax Evasin EV-3201V Ethylene-Vinyl Alcohol Copolymer
| Category | Polymer , Thermoplastic , Ethylene Vinyl Alcohol (EVOH) |
| Manufacturer | Gromax |
| Trade Name | Evasin |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax Evasin EV-3201V Ethylene-Vinyl Alcohol Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unmodified random Co-Polymer of [Ethylene-Vinyl alcohol], designed for therm-plastic processing into Sheets and Foils with high Oxygen and Aroma Barrier EffectInformation provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Water Vapor Transmission | 275 g/m²/day @Temperature 40.0 °C |
17.7 g/100 in²/day @Temperature 104 °F |
90% RH; ASTM E96 |
| Oxygen Transmission | 0.600 cc-mm/m²-24hr-atm @Temperature 25.0 °C |
1.52 cc-mil/100 in²-24hr-atm @Temperature 77.0 °F |
0% RH; ASTM D3985 |
| Viscosity | 1.09 cP @Temperature 230 °C |
1.09 cP @Temperature 446 °F |
?=200 sec<sup>-1</sup> |
| 1.33 cP @Temperature 230 °C |
1.33 cP @Temperature 446 °F |
?=100 sec<sup>-1</sup> | |
| 1.56 cP @Temperature 230 °C |
1.56 cP @Temperature 446 °F |
?=50 sec<sup>-1</sup> | |
| 1.75 cP @Temperature 210 °C |
1.75 cP @Temperature 410 °F |
?=200 sec<sup>-1</sup> | |
| 2.21 cP @Temperature 210 °C |
2.21 cP @Temperature 410 °F |
?=100 sec<sup>-1</sup> | |
| 2.68 cP @Temperature 210 °C |
2.68 cP @Temperature 410 °F |
?=50 sec<sup>-1</sup> | |
| 2.88 cP @Temperature 190 °C |
2.88 cP @Temperature 374 °F |
?=200 sec<sup>-1</sup> | |
| 3.73 cP @Temperature 190 °C |
3.73 cP @Temperature 374 °F |
?=100 sec<sup>-1</sup> | |
| 4.57 cP @Temperature 190 °C |
4.57 cP @Temperature 374 °F |
?=50 sec<sup>-1</sup> | |
| Melt Flow | 1.727 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.727 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
| 3.6762 g/10 min @Load 2.16 kg, Temperature 210 °C |
3.6762 g/10 min @Load 4.76 lb, Temperature 410 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 84 | 84 | ASTM D2240D |
| Tensile Strength at Break | 63.1 MPa | 9150 psi | ASTM D638 |
| Tensile Strength, Yield | 72.7 MPa | 10500 psi | ASTM D638 |
| Elongation at Break | 180 % | 180 % | ASTM D638 |
| Elongation at Yield | 5.6 % | 5.6 % | ASTM D638 |
| Tensile Modulus | 3.65 GPa | 529 ksi | ASTM D638 |
| Flexural Strength | 126.3 MPa | 18320 psi | ASTM D790 |
| Flexural Modulus | 4.32 GPa | 627 ksi | ASTM D790 |
| Izod Impact, Notched | >= 0.304 J/cm | >= 0.569 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 46.0 µm/m-°C | 25.6 µin/in-°F | below Tg |
| 56.0 µm/m-°C | 31.1 µin/in-°F | above Tg | |
| Melting Point | 184.86 °C | 364.75 °F | |
| Crystallization Temperature | 163 °C | 325 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.4 °C | 202 °F | ASTM D648 |
| Vicat Softening Point | 173.8 °C | 344.8 °F | JIS-K6742 |
| Glass Transition Temp, Tg | 73.9 °C | 165 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | <= 0.30 % | <= 0.30 % |