Grupo Repol Dinalon® B1S25 G35 35% Glass Fiber Reinforced Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Grupo Repol |
| Trade Name | Dinalon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Grupo Repol Dinalon® B1S25 G35 35% Glass Fiber Reinforced Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical properties are for dry as molded samples.Information provided by Grupo Repol.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183/A |
| Moisture Absorption at Equilibrium | <= 0.25 % | <= 0.25 % | Karl-Fischer; ISO 15512/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 185 MPa | 26800 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Flexural Strength | 290 MPa | 42100 psi | ISO 178 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75/A |
| Vicat Softening Point | >= 200 °C | >= 392 °F | 50 N; ISO 306 |