H.C. Starck F-21-5 Pure Molybdenum, Foil

Category Metal , Nonferrous Metal , Molybdenum Alloy , Refractory Metal , Pure Element
Manufacturer H.C. Starck
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF H.C. Starck F-21-5 Pure Molybdenum, Foil.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
F-21-5Description of Product: Rolled molybdenum foil from 0.001 inches through 0.0049 inches thick produced from pressed and sintered powder metallurgy sheet bar.Structure: All foil will be supplied in a stress-relieved condition.Information provided by H.C. Starck.
Mechanical Properties Metric English Comments
Tensile Strength >= 793 MPa

@Thickness <=0.0254 mm
 >= 115000 psi

@Thickness <=0.00100 in
 ASTM E-345
>= 793 MPa

@Thickness 0.0254 - 0.0508 mm
 >= 115000 psi

@Thickness 0.00100 - 0.00200 in
 ASTM E-345
>= 793 MPa

@Thickness 0.0508 - 0.0762 mm
 >= 115000 psi

@Thickness 0.00200 - 0.00300 in
 ASTM E-345
>= 793 MPa

@Thickness 0.0762 - 0.124 mm
 >= 115000 psi

@Thickness 0.00300 - 0.00490 in
 ASTM E-345
Tensile Strength, Yield >= 655 MPa

@Strain 0.200 %,
Thickness <=0.0254 mm
 >= 95000 psi

@Strain 0.200 %,
Thickness <=0.00100 in
 ASTM E-345
>= 655 MPa

@Strain 0.200 %,
Thickness 0.0254 - 0.0508 mm
 >= 95000 psi

@Strain 0.200 %,
Thickness 0.00100 - 0.00200 in
 ASTM E-345
>= 655 MPa

@Strain 0.200 %,
Thickness 0.0508 - 0.0762 mm
 >= 95000 psi

@Strain 0.200 %,
Thickness 0.00200 - 0.00300 in
 ASTM E-345
>= 655 MPa

@Strain 0.200 %,
Thickness 0.0762 - 0.124 mm
 >= 95000 psi

@Strain 0.200 %,
Thickness 0.00300 - 0.00490 in
 ASTM E-345
Elongation at Break >= 1.0 %

@Thickness 0.0254 - 0.0508 mm
 >= 1.0 %

@Thickness 0.00100 - 0.00200 in
 ASTM E-345
>= 2.0 %

@Thickness 0.0508 - 0.0762 mm
 >= 2.0 %

@Thickness 0.00200 - 0.00300 in
 ASTM E-345
>= 3.0 %

@Thickness 0.0762 - 0.124 mm
 >= 3.0 %

@Thickness 0.00300 - 0.00490 in
 ASTM E-345
Component Elements Properties Metric English Comments
Aluminum, Al <= 0.0020 %
<= 0.0020 %
Calcium, Ca <= 0.0030 %
<= 0.0030 %
Carbon, C <= 0.0050 %
<= 0.0050 %
Chromium, Cr <= 0.0050 %
<= 0.0050 %
Copper, Cu <= 0.0020 %
<= 0.0020 %
Iron, Fe <= 0.0050 %
<= 0.0050 %
Lead, Pb <= 0.0020 %
<= 0.0020 %
Magnesium, Mg <= 0.0010 %
<= 0.0010 %
Manganese, Mn <= 0.0010 %
<= 0.0010 %
Molybdenum, Mo >= 99.95 %
>= 99.95 %
by difference
Nickel, Ni <= 0.0020 %
<= 0.0020 %
Silicon, Si <= 0.0030 %
<= 0.0030 %
Tin, Sn <= 0.0030 %
<= 0.0030 %
Titanium, Ti <= 0.0020 %
<= 0.0020 %