HP Alloys Nitronic® 60 Austenitic Stainless, Level 5 Cold Worked

Category Metal , Ferrous Metal , Heat Resisting , Stainless Steel , T S20000 Series Stainless Steel
Manufacturer High Performance Alloys, Inc
Trade Name Nitronic®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF HP Alloys Nitronic® 60 Austenitic Stainless, Level 5 Cold Worked.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Level 5 Cold Worked applies to tensile properties of 0.25 to 1.5 in. sizes; other properties are typical of this alloy.Nitronic 60 is truly an all purpose metal. This fully austenitic alloy was originally designed as a high temperature alloy for temperatures around 1800ºF. The oxidation resistance of Nitronic 60 is similar to Type 309 S.S., and far superior to Type 304S.S. The additions of silicon and manganese have given the alloy a matrix to inhibit wear, galling, and fretting even in the annealed condition. Higher strengths are attainable through cold working the material and is still fully austenitic after severe cold-working. This working does not enhance the anti-galling properties as is normal for carbon steels and some stainless steels. The benefit to the cold or hot work put into the material is added strength and hardness. The chromium and nickel additions give it comparable corrosion to 304 and 316 stainless steels, while having approximately twice the yield strength. The high mechanical strength in annealed parts permits use of reduced cross sections for weight and cost reductions.Data provided by High Performance Alloys, Inc.
Physical Properties Metric English Comments
Density 7.62 g/cc
0.275 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate >= 1379 MPa
>= 200000 psi
Tensile Strength, Yield >= 1241 MPa

@Strain 0.200 %
>= 180000 psi

@Strain 0.200 %
Elongation at Break >= 10 %
>= 10 %
Reduction of Area >= 45 %
>= 45 %
Modulus of Elasticity 179 GPa
26000 ksi
In Tension
Poissons Ratio 0.30
0.30
Calculated
Shear Modulus 69.0 GPa
10000 ksi
Thermal Properties Metric English Comments
CTE, linear 15.8 µm/m-°C

@Temperature 20.0 - 95.0 °C
8.78 µin/in-°F

@Temperature 68.0 - 203 °F
Component Elements Properties Metric English Comments
Chromium, Cr 17 %
17 %
Iron, Fe 62 %
62 %
as balance
Manganese, Mn 8.0 %
8.0 %
Nickel, Ni 8.5 %
8.5 %
Nitrogen, N 0.14 %
0.14 %
Silicon, Si 4.0 %
4.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000130 ohm-cm
0.000130 ohm-cm