Hardwire 3S-23-12 High Density Composite

Category Metal , Ferrous Metal , Carbon Steel , High Carbon Steel , Metal Foam, Mesh, or Honeycomb
Manufacturer Hardwire, LLC
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hardwire 3S-23-12 High Density Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The 3S Hardwire is a high carbon steel cord with a micro-fine brass or AO-brass (Adhesion Optimized) coating. The 3S cord is used where balanced compressive and tensile strengths are required and represents the ultimate in economical value when measured in modulus per dollar. The 3S wire cord is made by twisting three identical wire filaments (All filaments are 0.0189 in diameter) together at a longer than usual lay length. The result is a cord with lower twist angles and straighter filaments that is the basis for the increased compressive strengths.Characteristics: 3S tapes have the highest compressive strengths of all Hardwire tapes and tend to match or exceed the tensile properties.Best value for stiffness per dollar as well as flexural and compressive strengths per dollar.The cords do not bloom in failure modes during compression or tension.Laminates exhibit steel like characteristics with high ductility and extreme deflection capability.Very high flexural strength as well as ductile failure modes (laminates tend to bend – not break).Tapes bend very easily and uniformly in standard sheet metal breaks.It is the boardiest of all Hardwire tapes – excellent for flat surfaces but still conformable enough for curved structures.All information provided by Hardwire, LLC.
Physical Properties Metric English Comments
Density 3.679 g/cc
0.1329 lb/in³
Laminate Density
Mechanical Properties Metric English Comments
Modulus of Elasticity 82.0 GPa
11900 ksi
Effective Modulus
Flexural Yield Strength 958 MPa
139000 psi
Sheet Stress