Haynes 556® alloy, bar after 16000 hours at 537°C

Category Metal , Superalloy , Iron Base
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes 556® alloy, bar after 16000 hours at 537°C.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists corrosion by molten chloride salts and is resistant to corrosion from molten zinc. Excellent forming and welding characteristics. Applications include tubing and structural members in municipal and industrial waste incinerators, rotary calciners and kilns for minerals processing, and non-rotating components in land-based gas turbines burning low-grade fuels; carbon regenerators, and in processes involving high-sulfur petroleum feedstocks; widely used for hot-dip galvanizing fixtures, spinners, and baskets, high speed furnace fans, air preheaters of diesel engines, the inner covers of coil annealing furnaces, and various high temperature applications in the aerospace industry.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.23 g/cc
0.297 lb/in³
at RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 660 MPa
95700 psi
Tensile Strength, Yield 260 MPa

@Strain 0.200 %
37700 psi

@Strain 0.200 %
Elongation at Break 48 %
48 %
in 50.8 mm
Modulus of Elasticity 205 GPa
29700 ksi
RT
138 GPa

@Temperature 1000 °C
20000 ksi

@Temperature 1830 °F
143 GPa

@Temperature 900 °C
20700 ksi

@Temperature 1650 °F
148 GPa

@Temperature 800 °C
21500 ksi

@Temperature 1470 °F
155 GPa

@Temperature 700 °C
22500 ksi

@Temperature 1290 °F
164 GPa

@Temperature 600 °C
23800 ksi

@Temperature 1110 °F
172 GPa

@Temperature 500 °C
24900 ksi

@Temperature 932 °F
179 GPa

@Temperature 400 °C
26000 ksi

@Temperature 752 °F
187 GPa

@Temperature 300 °C
27100 ksi

@Temperature 572 °F
195 GPa

@Temperature 200 °C
28300 ksi

@Temperature 392 °F
200 GPa

@Temperature 100 °C
29000 ksi

@Temperature 212 °F
Charpy Impact 240 J
177 ft-lb
Samples did not break. Average of 4 or more tests.
Thermal Properties Metric English Comments
CTE, linear 14.7 µm/m-°C

@Temperature 25.0 - 100 °C
8.17 µin/in-°F

@Temperature 77.0 - 212 °F
14.9 µm/m-°C

@Temperature 25.0 - 200 °C
8.28 µin/in-°F

@Temperature 77.0 - 392 °F
15.1 µm/m-°C

@Temperature 25.0 - 300 °C
8.39 µin/in-°F

@Temperature 77.0 - 572 °F
15.4 µm/m-°C

@Temperature 25.0 - 400 °C
8.56 µin/in-°F

@Temperature 77.0 - 752 °F
15.7 µm/m-°C

@Temperature 25.0 - 500 °C
8.72 µin/in-°F

@Temperature 77.0 - 932 °F
16.1 µm/m-°C

@Temperature 25.0 - 600 °C
8.94 µin/in-°F

@Temperature 77.0 - 1110 °F
16.4 µm/m-°C

@Temperature 25.0 - 700 °C
9.11 µin/in-°F

@Temperature 77.0 - 1290 °F
16.7 µm/m-°C

@Temperature 25.0 - 800 °C
9.28 µin/in-°F

@Temperature 77.0 - 1470 °F
17.0 µm/m-°C

@Temperature 25.0 - 900 °C
9.44 µin/in-°F

@Temperature 77.0 - 1650 °F
17.1 µm/m-°C

@Temperature 25.0 - 1000 °C
9.50 µin/in-°F

@Temperature 77.0 - 1830 °F
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
0.475 J/g-°C

@Temperature 100 °C
0.114 BTU/lb-°F

@Temperature 212 °F
0.493 J/g-°C

@Temperature 200 °C
0.118 BTU/lb-°F

@Temperature 392 °F
0.508 J/g-°C

@Temperature 300 °C
0.121 BTU/lb-°F

@Temperature 572 °F
0.523 J/g-°C

@Temperature 400 °C
0.125 BTU/lb-°F

@Temperature 752 °F
0.538 J/g-°C

@Temperature 500 °C
0.129 BTU/lb-°F

@Temperature 932 °F
0.552 J/g-°C

@Temperature 600 °C
0.132 BTU/lb-°F

@Temperature 1110 °F
0.561 J/g-°C

@Temperature 700 °C
0.134 BTU/lb-°F

@Temperature 1290 °F
0.570 J/g-°C

@Temperature 800 °C
0.136 BTU/lb-°F

@Temperature 1470 °F
0.595 J/g-°C

@Temperature 900 °C
0.142 BTU/lb-°F

@Temperature 1650 °F
0.618 J/g-°C

@Temperature 1000 °C
0.148 BTU/lb-°F

@Temperature 1830 °F
0.638 J/g-°C

@Temperature 1100 °C
0.152 BTU/lb-°F

@Temperature 2010 °F
Thermal Conductivity 11.1 W/m-K
77.0 BTU-in/hr-ft²-°F
RT
13.1 W/m-K

@Temperature 100 °C
90.9 BTU-in/hr-ft²-°F

@Temperature 212 °F
15.4 W/m-K

@Temperature 200 °C
107 BTU-in/hr-ft²-°F

@Temperature 392 °F
17.3 W/m-K

@Temperature 300 °C
120 BTU-in/hr-ft²-°F

@Temperature 572 °F
19.0 W/m-K

@Temperature 400 °C
132 BTU-in/hr-ft²-°F

@Temperature 752 °F
20.8 W/m-K

@Temperature 500 °C
144 BTU-in/hr-ft²-°F

@Temperature 932 °F
22.4 W/m-K

@Temperature 600 °C
155 BTU-in/hr-ft²-°F

@Temperature 1110 °F
24.0 W/m-K

@Temperature 700 °C
167 BTU-in/hr-ft²-°F

@Temperature 1290 °F
25.5 W/m-K

@Temperature 800 °C
177 BTU-in/hr-ft²-°F

@Temperature 1470 °F
27.2 W/m-K

@Temperature 900 °C
189 BTU-in/hr-ft²-°F

@Temperature 1650 °F
28.9 W/m-K

@Temperature 1000 °C
201 BTU-in/hr-ft²-°F

@Temperature 1830 °F
30.4 W/m-K

@Temperature 1100 °C
211 BTU-in/hr-ft²-°F

@Temperature 2010 °F
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Solidus 1330 °C
2430 °F
Liquidus 1415 °C
2579 °F
Component Elements Properties Metric English Comments
Aluminum, Al 0.20 %
0.20 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000952 ohm-cm
0.0000952 ohm-cm
RT
0.0000986 ohm-cm

@Temperature 100 °C
0.0000986 ohm-cm

@Temperature 212 °F
0.0001026 ohm-cm

@Temperature 200 °C
0.0001026 ohm-cm

@Temperature 392 °F
0.0001065 ohm-cm

@Temperature 300 °C
0.0001065 ohm-cm

@Temperature 572 °F
0.0001095 ohm-cm

@Temperature 400 °C
0.0001095 ohm-cm

@Temperature 752 °F
0.0001125 ohm-cm

@Temperature 500 °C
0.0001125 ohm-cm

@Temperature 932 °F
0.0001151 ohm-cm

@Temperature 600 °C
0.0001151 ohm-cm

@Temperature 1110 °F
0.0001172 ohm-cm

@Temperature 700 °C
0.0001172 ohm-cm

@Temperature 1290 °F
0.000119 ohm-cm

@Temperature 800 °C
0.000119 ohm-cm

@Temperature 1470 °F
0.0001207 ohm-cm

@Temperature 900 °C
0.0001207 ohm-cm

@Temperature 1650 °F
0.0001223 ohm-cm

@Temperature 1000 °C
0.0001223 ohm-cm

@Temperature 1830 °F
0.0001237 ohm-cm

@Temperature 1100 °C
0.0001237 ohm-cm

@Temperature 2010 °F