- Haynes Hastelloy® W alloy as a weld filler, base metal Multimet alloy 12.7 mm plate weldment
Haynes Hastelloy® W alloy as a weld filler, base metal Multimet alloy 12.7 mm plate weldment
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Haynes International, Inc. |
| Trade Name | Hastelloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Haynes Hastelloy® W alloy as a weld filler, base metal Multimet alloy 12.7 mm plate weldment.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemical process industries.Data provided by the manufacturer, Haynes International, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 9.00 g/cc | 0.325 lb/in³ | at RT |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 800 MPa | 116000 psi | |
| 290 MPa @Temperature 870 °C |
42100 psi @Temperature 1600 °F |
||
| Tensile Strength, Yield | 425 MPa | 61600 psi | |
| 215 MPa @Temperature 870 °C |
31200 psi @Temperature 1600 °F |
||
| Elongation at Break | 49 % | 49 % | Failures in base metal. |
| 28 % @Temperature 870 °C |
28 % @Temperature 1600 °F |
Failures in base metal. | |
| Reduction of Area | 65 % | 65 % | Failures in base metal. |
| 42 % @Temperature 870 °C |
42 % @Temperature 1600 °F |
Failures in base metal. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| 13.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.33 µin/in-°F @Temperature 68.0 - 932 °F |
||
| 13.5 µm/m-°C @Temperature 20.0 - 700 °C |
7.50 µin/in-°F @Temperature 68.0 - 1290 °F |
||
| 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
||
| 14.8 µm/m-°C @Temperature 20.0 - 900 °C |
8.22 µin/in-°F @Temperature 68.0 - 1650 °F |
||
| 15.3 µm/m-°C @Temperature 20.0 - 1000 °C |
8.50 µin/in-°F @Temperature 68.0 - 1830 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.12 % | <= 0.12 % | |
| Chromium, Cr | 5.0 % | 5.0 % | |
| Cobalt, Co | 2.5 % | 2.5 % | |
| Iron, Fe | 6.0 % | 6.0 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Molybdenum, Mo | 24 % | 24 % | |
| Nickel, Ni | 63 % | 63 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Vanadium, V | <= 0.60 % | <= 0.60 % |