Hexcel® F515 Epoxy Resin, TXX200 Carbon Tape

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite
Manufacturer Hexcel
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® F515 Epoxy Resin, TXX200 Carbon Tape.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
STD MOD FiberInformation provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 1482 MPa

@Temperature 71.0 °C
 214900 psi

@Temperature 160 °F
 1/2 hr
1717 MPa

@Temperature 23.0 °C
 249000 psi

@Temperature 73.4 °F
Tensile Modulus 108.9 GPa

@Temperature 71.0 °C
 15790 ksi

@Temperature 160 °F
 1/2 hr
110.3 GPa

@Temperature 23.0 °C
 16000 ksi

@Temperature 73.4 °F
Flexural Yield Strength 1289 MPa

@Temperature 71.0 °C
 187000 psi

@Temperature 160 °F
 1/2 hr
1558 MPa

@Temperature 23.0 °C
 226000 psi

@Temperature 73.4 °F
Flexural Modulus 124.8 GPa

@Temperature 71.0 °C
 18100 ksi

@Temperature 160 °F
 1/2 hr
125.5 GPa

@Temperature 23.0 °C
 18200 ksi

@Temperature 73.4 °F
Compressive Yield Strength 1158 MPa

@Temperature 71.0 °C
 168000 psi

@Temperature 160 °F
 1/2 hr
1303 MPa

@Temperature 23.0 °C
 189000 psi

@Temperature 73.4 °F
Compressive Modulus 112.4 GPa

@Temperature 71.0 °C
 16300 ksi

@Temperature 160 °F
 1/2 hr
117.9 GPa

@Temperature 23.0 °C
 17100 ksi

@Temperature 73.4 °F
Shear Strength 69.6 MPa

@Temperature 71.0 °C
 10100 psi

@Temperature 160 °F
 Short Beam, 1/2 hr
86.9 MPa

@Temperature 23.0 °C
 12600 psi

@Temperature 73.4 °F