- Hexcel® HexPly® 922-1/35%/G926 180°C Curing Epoxy Matrix
Hexcel® HexPly® 922-1/35%/G926 180°C Curing Epoxy Matrix
| Category | Polymer , Thermoset , Epoxy , Epoxy Cure Resin |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® 922-1/35%/G926 180°C Curing Epoxy Matrix.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
5H satin/370g/m2 carbon fabric: FVC=60%Information provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 718 MPa | 104000 psi | Material as cured; RT |
| 786 MPa | 114000 psi | After ageing at 70°C / 95% RH; RT | |
| 677 MPa @Temperature 175 °C |
98200 psi @Temperature 347 °F |
After ageing at 70°C / 95% RH | |
| 774 MPa @Temperature 175 °C |
112000 psi @Temperature 347 °F |
Material as cured | |
| Tensile Modulus | 67.0 GPa | 9720 ksi | Material as cured; RT |
| 77.0 GPa | 11200 ksi | After ageing at 70°C / 95% RH; RT | |
| 64.0 GPa @Temperature 175 °C |
9280 ksi @Temperature 347 °F |
After ageing at 70°C / 95% RH | |
| 70.0 GPa @Temperature 175 °C |
10200 ksi @Temperature 347 °F |
Material as cured | |
| Flexural Yield Strength | 1038 MPa | 150500 psi | After ageing at 70°C / 95% RH; RT |
| 1079 MPa | 156500 psi | Material as cured; RT | |
| 244 MPa @Temperature 175 °C |
35400 psi @Temperature 347 °F |
After ageing at 70°C / 95% RH | |
| 761 MPa @Temperature 175 °C |
110000 psi @Temperature 347 °F |
Material as cured | |
| Flexural Modulus | 57.0 GPa | 8270 ksi | After ageing at 70°C / 95% RH; RT |
| 60.0 GPa | 8700 ksi | Material as cured; RT | |
| 42.0 GPa @Temperature 175 °C |
6090 ksi @Temperature 347 °F |
After ageing at 70°C / 95% RH | |
| 56.0 GPa @Temperature 175 °C |
8120 ksi @Temperature 347 °F |
Material as cured | |
| Compressive Yield Strength | 605 MPa | 87700 psi | After ageing at 70°C / 95% RH; RT |
| 667 MPa | 96700 psi | Material as cured; RT | |
| 218 MPa @Temperature 175 °C |
31600 psi @Temperature 347 °F |
After ageing at 70°C / 95% RH | |
| 493 MPa @Temperature 175 °C |
71500 psi @Temperature 347 °F |
Material as cured | |
| Compressive Modulus | 65.0 GPa | 9430 ksi | After ageing at 70°C / 95% RH; RT |
| 66.0 GPa | 9570 ksi | Material as cured; RT | |
| 52.0 GPa @Temperature 175 °C |
7540 ksi @Temperature 347 °F |
After ageing at 70°C / 95% RH | |
| 57.0 GPa @Temperature 175 °C |
8270 ksi @Temperature 347 °F |
Material as cured | |
| Shear Modulus | 5.00 GPa | 725 ksi | In-Plane; After ageing at 70°C / 95% RH; RT |
| 5.60 GPa | 812 ksi | In-Plane; Material as cured; RT | |
| Shear Strength | 73.0 MPa | 10600 psi | IL; Material as cured; RT |
| 79.0 MPa | 11500 psi | IL; After ageing at 70°C / 95% RH; RT | |
| 90.0 MPa | 13100 psi | In-Plane; After ageing at 70°C / 95% RH; RT | |
| 98.0 MPa | 14200 psi | In-Plane; Material as cured; RT | |
| 20.0 MPa @Temperature 175 °C |
2900 psi @Temperature 347 °F |
IL; After ageing at 70°C / 95% RH | |
| 53.0 MPa @Temperature 175 °C |
7690 psi @Temperature 347 °F |
IL; Material as cured |