Hexcel® HexPly® EF01 Epoxy Curing System after THR 120 EF01 S25 38% Curing Cycle

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® EF01 Epoxy Curing System after THR 120 EF01 S25 38% Curing Cycle.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by HexCel
Mechanical Properties Metric English Comments
Flexural Yield Strength 1320.9 MPa

@Temperature 50.0 °C
 191580 psi

@Temperature 122 °F
 Flexure Long; 15 min @ 250°F; prEN 2563
1351.0 MPa

@Temperature 50.0 °C
 195940 psi

@Temperature 122 °F
 Flexure Long; 30 min @ 250°F; prEN 2563
1381.0 MPa

@Temperature 50.0 °C
 200290 psi

@Temperature 122 °F
 Flexure Long; 10 min @ 250°F; prEN 2563
1551.0 MPa

@Temperature 22.8 °C
 224960 psi

@Temperature 73.0 °F
 Flexure Long; 15 min @ 250°F; prEN 2563
1561.1 MPa

@Temperature 22.8 °C
 226420 psi

@Temperature 73.0 °F
 Flexure Long; 30 min @ 250°F; prEN 2563
1601.1 MPa

@Temperature 22.8 °C
 232220 psi

@Temperature 73.0 °F
 Flexure Long; 10 min @ 250°F; prEN 2563
Flexural Modulus 106.0 GPa

@Temperature 50.0 °C
 15380 ksi

@Temperature 122 °F
 Flexure Long; 15 min @ 250°F; prEN 2563
108.0 GPa

@Temperature 22.8 °C
 15670 ksi

@Temperature 73.0 °F
 Flexure Long; 15 min @ 250°F; prEN 2563
108.0 GPa

@Temperature 22.8 °C
 15670 ksi

@Temperature 73.0 °F
 Flexure Long; 30 min @ 250°F; prEN 2563
108.0 GPa

@Temperature 50.0 °C
 15670 ksi

@Temperature 122 °F
 Flexure Long; 30 min @ 250°F; prEN 2563
109.1 GPa

@Temperature 22.8 °C
 15820 ksi

@Temperature 73.0 °F
 Flexure Long; 10 min @ 250°F; prEN 2563
109.1 GPa

@Temperature 50.0 °C
 15820 ksi

@Temperature 122 °F
 Flexure Long; 10 min @ 250°F; prEN 2563
Shear Strength 71.0 MPa

@Temperature 50.0 °C
 10300 psi

@Temperature 122 °F
 ILSS Weft; 10 min @ 250°F
71.0 MPa

@Temperature 50.0 °C
 10300 psi

@Temperature 122 °F
 ILSS Weft; 15 min @ 250°F
71.0 MPa

@Temperature 50.0 °C
 10300 psi

@Temperature 122 °F
 ILSS Weft; 30 min @ 250°F
86.05 MPa

@Temperature 22.8 °C
 12480 psi

@Temperature 73.0 °F
 ILSS Long; 10 min @ 250°F
86.05 MPa

@Temperature 22.8 °C
 12480 psi

@Temperature 73.0 °F
 ILSS Long; 30 min @ 250°F
87.08 MPa

@Temperature 22.8 °C
 12630 psi

@Temperature 73.0 °F
 ILSS Long; 15 min @ 250°F