| Category | Polymer , Thermoset , Polyimide, TS |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® F650 Bismaleimide Resin with Quartz 581 fabric reinforcement.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Laminate Physicals: 55.4% Fiber volume, 31.4% Resin content, 0.7% Voids, 1.78% gm.cc Specific gravityInformation provided by HexCel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.78 g/cc | 1.78 g/cc |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 433 MPa @Temperature 232 °C |
62800 psi @Temperature 450 °F |
|
| 459.2 MPa @Temperature 177 °C |
66600 psi @Temperature 351 °F |
||
| 531.6 MPa @Temperature 23.0 °C |
77100 psi @Temperature 73.4 °F |
||
| Tensile Modulus | 24.8 GPa @Temperature 177 °C |
3600 ksi @Temperature 351 °F |
|
| 26.9 GPa @Temperature 23.0 °C |
3900 ksi @Temperature 73.4 °F |
||
| Compressive Yield Strength | 292.3 MPa @Temperature 232 °C |
42390 psi @Temperature 450 °F |
|
| 375.8 MPa @Temperature 177 °C |
54510 psi @Temperature 351 °F |
||
| 504.7 MPa @Temperature 23.0 °C |
73200 psi @Temperature 73.4 °F |
||
| Compressive Modulus | 26.5 GPa @Temperature 177 °C |
3840 ksi @Temperature 351 °F |
|
| 28.0 GPa @Temperature 23.0 °C |
4060 ksi @Temperature 73.4 °F |
||
| Shear Strength | 42.1 MPa @Temperature 232 °C |
6110 psi @Temperature 450 °F |
|
| 49.6 MPa @Temperature 177 °C |
7190 psi @Temperature 351 °F |
||
| 60.7 MPa @Temperature 23.0 °C |
8800 psi @Temperature 73.4 °F |