Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, 37%/7781 Fiber

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, 37%/7781 Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by HexCel
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
Resin Density
2.60 g/cc
0.0939 lb/in³
Fibre Density
Mechanical Properties Metric English Comments
Tensile Strength, Yield 415 MPa
60200 psi
90º, RT, Dry; EN2561
510 MPa
74000 psi
RT; Dry; EN2561
270 MPa

@Temperature 75.0 °C
39200 psi

@Temperature 167 °F
Wet; EN2561
270 MPa

@Temperature 100 °C
39200 psi

@Temperature 212 °F
Wet; EN2561
270 MPa

@Temperature 75.0 °C
39200 psi

@Temperature 167 °F
90º, Wet; EN2561
300 MPa

@Temperature 100 °C
43500 psi

@Temperature 212 °F
90º, Wet; EN2561
Tensile Modulus 26.0 GPa
3770 ksi
90º, RT, Dry; EN2561
29.0 GPa
4210 ksi
RT; Dry; EN2561
25.0 GPa

@Temperature 100 °C
3630 ksi

@Temperature 212 °F
90º, Wet; EN2561
26.0 GPa

@Temperature 75.0 °C
3770 ksi

@Temperature 167 °F
90º, Wet; EN2561
27.0 GPa

@Temperature 100 °C
3920 ksi

@Temperature 212 °F
Wet; EN2561
28.0 GPa

@Temperature 75.0 °C
4060 ksi

@Temperature 167 °F
Wet; EN2561
Compressive Yield Strength 460 MPa
66700 psi
90º, RT, Dry; DIN65380
500 MPa
72500 psi
RT; Dry; DIN65380
320 MPa

@Temperature 100 °C
46400 psi

@Temperature 212 °F
90º, Wet; DIN65380
360 MPa

@Temperature 100 °C
52200 psi

@Temperature 212 °F
Wet; DIN65380
380 MPa

@Temperature 75.0 °C
55100 psi

@Temperature 167 °F
Wet; DIN65380
400 MPa

@Temperature 75.0 °C
58000 psi

@Temperature 167 °F
90º, Wet; DIN65380
Compressive Modulus 27.0 GPa
3920 ksi
90º, RT, Dry; DIN65380
30.0 GPa
4350 ksi
RT; Dry; DIN65380
25.0 GPa

@Temperature 100 °C
3630 ksi

@Temperature 212 °F
90º, Wet; DIN65380
26.0 GPa

@Temperature 75.0 °C
3770 ksi

@Temperature 167 °F
Wet; DIN65380
26.0 GPa

@Temperature 100 °C
3770 ksi

@Temperature 212 °F
Wet; DIN65380
26.0 GPa

@Temperature 75.0 °C
3770 ksi

@Temperature 167 °F
90º, Wet; DIN65380
Shear Strength 80.0 MPa
11600 psi
In-Plane, RT, Dry; EN6031
83.0 MPa
12000 psi
0º, ILSS (Short Beam), RT, Dry; EN2563
37.0 MPa

@Temperature 100 °C
5370 psi

@Temperature 212 °F
0º, ILSS (Short Beam), Wet; EN2563
43.0 MPa

@Temperature 75.0 °C
6240 psi

@Temperature 167 °F
0º, ILSS (Short Beam), Wet; EN2563
70.0 MPa

@Temperature 100 °C
10200 psi

@Temperature 212 °F
In-Plane, Wet; EN6031
75.0 MPa

@Temperature 75.0 °C
10900 psi

@Temperature 167 °F
In-Plane, Wet; EN6031
Processing Properties Metric English Comments
Shelf Life 14.0 Month

@Temperature -18.0 °C
14.0 Month

@Temperature -0.400 °F
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.23