Hexcel® HexPly® M35-4 80-180°C Curing Epoxy Matrix, M35-4/40%/48280/1000 Fabric

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® M35-4 80-180°C Curing Epoxy Matrix, M35-4/40%/48280/1000 Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fiber: T1000 12K 5H Satin, 283 g/m2Information provided by HexCel
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
Nominal Laminate Density
Mechanical Properties Metric English Comments
Tensile Strength, Yield 1425 MPa

@Temperature 23.0 °C
 206700 psi

@Temperature 73.4 °F
 prEN2561 Type B
Tensile Modulus 89.0 GPa

@Temperature 23.0 °C
 12900 ksi

@Temperature 73.4 °F
 prEN2561 Type B
Compressive Yield Strength 925 MPa

@Temperature 23.0 °C
 134000 psi

@Temperature 73.4 °F
 prEN2580 Type A
Shear Modulus 4.70 GPa

@Temperature 23.0 °C
 682 ksi

@Temperature 73.4 °F
 In-Plane; prEN6032
Shear Strength 43.0 MPa

@Temperature 140 °C
 6240 psi

@Temperature 284 °F
 ILSS; prEN2563
50.0 MPa

@Temperature 80.0 °C
 7250 psi

@Temperature 176 °F
 ILSS; prEN2563
51.0 MPa

@Temperature 23.0 °C
 7400 psi

@Temperature 73.4 °F
 ILSS; prEN2563
52.0 MPa

@Temperature 100 °C
 7540 psi

@Temperature 212 °F
 ILSS; prEN2563
54.0 MPa

@Temperature 120 °C
 7830 psi

@Temperature 248 °F
 ILSS; prEN2563
118 MPa

@Temperature 23.0 °C
 17100 psi

@Temperature 73.4 °F
 In-Plane; prEN6032
Processing Properties Metric English Comments
Shelf Life >= 12.0 Month

@Temperature -18.0 °C
 >= 12.0 Month

@Temperature -0.400 °F
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.0308
Fiber Volume (%) 51