Hexcel® HexPly® M35-4 80-180°C Curing Epoxy Matrix, M35-4/40%/G1089/1000 Fabric

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® M35-4 80-180°C Curing Epoxy Matrix, M35-4/40%/G1089/1000 Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fiber: T800H 6K 2x2 Twill, 200 g/m2Information provided by HexCel
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
Nominal Laminate Density
Mechanical Properties Metric English Comments
Tensile Strength, Yield 1017 MPa

@Temperature 23.0 °C
 147500 psi

@Temperature 73.4 °F
 prEN2561 Type B
Tensile Modulus 86.0 GPa

@Temperature 23.0 °C
 12500 ksi

@Temperature 73.4 °F
 prEN2561 Type B
Compressive Yield Strength 904 MPa

@Temperature 23.0 °C
 131000 psi

@Temperature 73.4 °F
 prEN2580 Type A
Compressive Modulus 74.0 GPa
10700 ksi
23; prEN2580 Type A
Shear Modulus 5.20 GPa

@Temperature 23.0 °C
 754 ksi

@Temperature 73.4 °F
 In-Plane; prEN6032
Shear Strength 44.0 MPa

@Temperature 140 °C
 6380 psi

@Temperature 284 °F
 ILSS; prEN2563
52.0 MPa

@Temperature 120 °C
 7540 psi

@Temperature 248 °F
 ILSS; prEN2563
61.0 MPa

@Temperature 100 °C
 8850 psi

@Temperature 212 °F
 ILSS; prEN2563
67.0 MPa

@Temperature 80.0 °C
 9720 psi

@Temperature 176 °F
 ILSS; prEN2563
71.0 MPa

@Temperature 23.0 °C
 10300 psi

@Temperature 73.4 °F
 ILSS; prEN2563
124 MPa

@Temperature 23.0 °C
 18000 psi

@Temperature 73.4 °F
 In-Plane; prEN6032
Processing Properties Metric English Comments
Shelf Life >= 12.0 Month

@Temperature -18.0 °C
 >= 12.0 Month

@Temperature -0.400 °F
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.0217
Fiber Volume (%) 50.9