Hexcel® HexPly® M49 120°C Curing Epoxy Matrix, 6K High Strength Carbon

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® M49 120°C Curing Epoxy Matrix, 6K High Strength Carbon.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fiber Designation: C370S5, Satin weave, 5HInformation provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 741 MPa

@Temperature 23.0 °C
 107000 psi

@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D3039
Tensile Modulus 54.0 GPa

@Temperature 23.0 °C
 7830 ksi

@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D3039
Flexural Yield Strength 518 MPa

@Temperature 90.0 °C
 75100 psi

@Temperature 194 °F
 0°, Conditioning: 23°C; ASTM D790
921 MPa

@Temperature 23.0 °C
 134000 psi

@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D790
Flexural Modulus 37.0 GPa

@Temperature 90.0 °C
 5370 ksi

@Temperature 194 °F
 0°, Conditioning: 23°C; ASTM D790
41.0 GPa

@Temperature 23.0 °C
 5950 ksi

@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D790
Compressive Yield Strength 350 MPa

@Temperature 90.0 °C
 50800 psi

@Temperature 194 °F
 0°, Conditioning: 23°C; ASTM D965
610 MPa

@Temperature 23.0 °C
 88500 psi

@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D965
Shear Strength 29.0 MPa

@Temperature 60.0 °C
 4210 psi

@Temperature 140 °F
 0°, Interlaminar, Conditioning: 60°C-90% RH; ASTM D2344
36.0 MPa

@Temperature 90.0 °C
 5220 psi

@Temperature 194 °F
 0°, Interlaminar, Conditioning: 23°C; ASTM D2344
69.0 MPa

@Temperature 23.0 °C
 10000 psi

@Temperature 73.4 °F
 0°, Interlaminar, Conditioning: 23°C; ASTM D2344
Processing Properties Metric English Comments
Shelf Life 12.0 Month

@Temperature -18.0 °C
 12.0 Month

@Temperature -0.400 °F
Descriptive Properties Value Comments
Dry Resin Content (%) 42
Fiber Volume (%) 49.5