Hexcel® HexWeb® CR-PAA™ 3/8-5056-0.0015 Phosphoric Acid Anodized Aluminum Honeycomb

Category Metal , Metal Foam, Mesh, or Honeycomb , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Hexcel
Trade Name HexWeb®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® CR-PAA™ 3/8-5056-0.0015 Phosphoric Acid Anodized Aluminum Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the face sheets that carry bending loads and the honeycomb that carries the shear loads. The adhesive is the interface between the facing and the core in the same way that the oxide on the aluminum and the primer that has been applied to it is the interface between the honeycomb substrate material and the bonding adhesive. This interface is critical to the performance of honeycomb bonded assemblies.Information provided by HexCel
Physical Properties Metric English Comments
Density 0.0368 g/cc
0.00133 lb/in³
Nominal
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 1.07 MPa
>= 155 psi
Bare, min
>= 1.07 MPa
>= 155 psi
Stabilized, min
1.48 MPa
215 psi
Bare, typ
1.55 MPa
225 psi
Stabilized, typ
Compressive Modulus 0.400 GPa
58.0 ksi
Stabilized, typ
Shear Modulus 0.103 GPa
15.0 ksi
Plate Shear, W Direction, typ
0.221 GPa
32.0 ksi
Plate Shear, L Direction, typ
Shear Strength >= 0.427 MPa
>= 62.0 psi
Plate Shear, W Direction, min
0.655 MPa
95.0 psi
Plate Shear, W Direction, typ
>= 0.896 MPa
>= 130 psi
Plate Shear, L Direction, min
1.17 MPa
170 psi
Plate Shear, L Direction, typ