Hexcel® HexWeb® HRH-10 - 3/8 - 2.0 Aramid Fiber/Phenolic Resin Honeycomb

Category	Other Engineering Material , Composite Core Material , Composite Fibers , Polymer , Thermoset , Aramid , Phenolic
Manufacturer	Hexcel
Trade Name	HexWeb®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Hexcel® HexWeb® HRH-10 - 3/8 - 2.0 Aramid Fiber/Phenolic Resin Honeycomb.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the hexagonal or OX-Core confiation, the block is dipped in phenolic resin. After curing the resin, slices are cut to the desired thickness. For special applications, such as air directionalizing, HexWeb HRH-10 can be provided without the phenolic resin. Using this process, a wide range of cell sizes, paper thicknesses, and densities can be produced.Information provided by HexCel

Physical Properties	Metric	English	Comments
Density	0.0320 g/cc	0.00116 lb/in³

Mechanical Properties	Metric	English	Comments
Compressive Yield Strength	>= 0.793 MPa	>= 115 psi	Bare, min
	>= 0.862 MPa	>= 125 psi	Stabilized, min
	0.965 MPa	140 psi	Bare, typ
	1.07 MPa	155 psi	Stabilized, typ
Compressive Modulus	0.0758 GPa	11.0 ksi	Stabilized, typ
Shear Modulus	0.0165 GPa	2.40 ksi	Plate Shear, W Direction, typ
	0.0255 GPa	3.70 ksi	Plate Shear, L Direction, typ
Shear Strength	>= 0.248 MPa	>= 36.0 psi	Plate Shear, W Direction, min
	0.379 MPa	55.0 psi	Plate Shear, W Direction, typ
	>= 0.496 MPa	>= 72.0 psi	Plate Shear, L Direction, min
	0.621 MPa	90.0 psi	Plate Shear, L Direction, typ