Hexcel® HexWeb® HRP/OX - 3/8 - 5.5 Fiberglass/Phenolic Honeycomb

Category Ceramic , Glass , Glass Fiber , Other Engineering Material , Composite Core Material , Composite Fibers , Polymer , Thermoset , Phenolic
Manufacturer Hexcel
Trade Name HexWeb®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® HRP/OX - 3/8 - 5.5 Fiberglass/Phenolic Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation: Material-Cell Size (inches)-DensityHexWeb HRP is a glass fabric reinforced honeycomb in which a heat-resistant phenolic resin is used both for initial and final impregnations. This product was developed for use at service temperatures up to 350°F. However, it is also well suited for short exposures at high temperatures. The HexWeb HRP-series honeycomb is available in the standard hexagonal confiation, as well as in the two formale geometries - OX-Core and Flex-Core.Features: High strength up to 350°F; Good insulation and dielectric properties; Good bonding surface; Readily heat formed.Applications: HexWeb HRP has proven to be an excellent core material for radomes, aircraft structural parts and fairings, heat shields, and other assemblies that see elevated temperature service.
Physical Properties Metric English Comments
Density 0.0881 g/cc
0.00318 lb/in³
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 4.00 MPa
>= 580 psi
Bare, min
>= 4.24 MPa
>= 615 psi
Stabilized, min
4.83 MPa
700 psi
Bare, typ
5.65 MPa
820 psi
Stabilized, typ
Compressive Modulus 0.414 GPa
60.0 ksi
Stabilized, typ
Shear Modulus 0.0689 GPa
10.0 ksi
Plate Shear, L Direction, typ
0.117 GPa
17.0 ksi
Plate Shear, W Direction, typ
Shear Strength >= 1.45 MPa
>= 210 psi
Plate Shear, L Direction, min
1.86 MPa
270 psi
Plate Shear, L Direction, typ
>= 1.90 MPa
>= 275 psi
Plate Shear, W Direction, min
2.45 MPa
355 psi
Plate Shear, W Direction, typ
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 177 °C
350 °F
High strength retained