Hexcel® Redux® 382H (0.06 psf) Film Adhesive

Category Polymer , Adhesive , Film , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Hexcel
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® Redux® 382H (0.06 psf) Film Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Redux 382H is a 250°F curing modified epoxy film adhesive available in both supported and unsupported versions. Redux 382H is a versatile adhesive system suitable for bonding a wide variety of substrates with various temperature cure cycles.Features: Superior bonding capability on substrates with high moisture contents; Low volatile content allows use with perforated and non-perforated core materials; Excellent environmental resistance when tested to US-Military Specification MMM-A-132; Handling characteristics minimize shop handling and lay up times; Meets requirements of US Specifications: MMM-A-132, MILK-A-25462, and ASTM-E865-82.Applications: Redux 382H is adaptable to high and low temperature cure cycles normally associated with large scale metal to metal and sandwich panel bonding. Redux 382H gives superior mechanical properties on metal, wood and paper substrates.
Physical Properties Metric English Comments
Storage Temperature -17.8 °C
0.000 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 5.86 MPa

@Temperature 82.2 °C
850 psi

@Temperature 180 °F
Flatwise Tensile, Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463.
7.58 MPa

@Temperature -55.0 °C
1100 psi

@Temperature -67.0 °F
Flatwise Tensile, Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463.
8.27 MPa

@Temperature 21.1 °C
1200 psi

@Temperature 70.0 °F
Flatwise Tensile, Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463.
Shear Strength 17.9 MPa

@Temperature 100 °C
2600 psi

@Temperature 212 °F
Lap Shear, Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463.
26.9 MPa

@Temperature 82.2 °C
3900 psi

@Temperature 180 °F
Lap Shear, Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463.
31.0 MPa

@Temperature -55.0 °C
4500 psi

@Temperature -67.0 °F
Lap Shear, Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463.
32.8 MPa

@Temperature 21.1 °C
4750 psi

@Temperature 70.0 °F
Lap Shear, Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463, Exposure: 30 days in tap water.
32.8 MPa

@Temperature 21.1 °C
4750 psi

@Temperature 70.0 °F
Lap Shear, Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463, Exposure: 30 days at 120°F (95% rH).
33.8 MPa

@Temperature 21.1 °C
4900 psi

@Temperature 70.0 °F
Lap Shear, Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463, Exposure: 30 days salt spray.
34.5 MPa

@Temperature 21.1 °C
5000 psi

@Temperature 70.0 °F
Lap Shear, Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463.
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature -17.8 °C
6.00 Month

@Temperature 0.000 °F
Descriptive Properties Value Comments
Areal Weight (psf) 0.06
Climbing Drum Peel (in-lb/3in) 44
-67°F; Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463.
52
180°F; Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463.
60
70°F;Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463.
Roll Width (in) 49
Standard Roll (ft2) 670