Hexcel® Redux® HP655 Toughened BMI film Adhesive

Category Polymer , Adhesive , Film
Manufacturer Hexcel
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® Redux® HP655 Toughened BMI film Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Redux® HP655 is a toughened BMI structural adhesive designed for metal to metal, composite to composite, and honeycomb sandwich bonding for both co-cured and precured composite skins. Redux® HP655 combines high fracture toughness and high shear with good peel strengths. Recommended service temperature is up to 350°F wet and 460°F dry. Redux® HP655 was developed to be compatible with Hexcel's entire BMI prepreg product line.Features: Good co-cure potential with Hexcel's BMI prepreg range; Excellent hot lap shear performance; Good fracture toughness; Low volatile content and low out-gassing properties; Available with or without a woven glass carrier.Applications: Metal to metal bonding; Composite to composite bonding; Sandwich constructions.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 8.07 MPa
1170 psi
Neat Resin, RT
5.00 MPa

@Temperature 21.1 °C
 725 psi

@Temperature 70.0 °F
 Flatwise Tensile; After 500 hrs at 400°F (Weight loss = 0.75%); Composite Honeycomb Sandwich Performance; ASTM C 297
5.10 MPa

@Temperature -55.0 °C
 740 psi

@Temperature -67.0 °F
 Flatwise Tensile; 2.52" Cell; Aluminum Honeycomb Sandwich Performance; ASTM C 297
5.10 MPa

@Temperature 21.1 °C
 740 psi

@Temperature 70.0 °F
 Flatwise Tensile; 2.52" Cell; Aluminum Honeycomb Sandwich Performance; ASTM C 297
>= 5.17 MPa

@Temperature 204 °C
 >= 750 psi

@Temperature 400 °F
 Flatwise Tensile; After 500 hrs at 400°F (Weight loss = 0.75%); Composite Honeycomb Sandwich Performance; ASTM C 297
5.38 MPa

@Temperature 204 °C
 780 psi

@Temperature 400 °F
 Flatwise Tensile; 2.52" Cell; Aluminum Honeycomb Sandwich Performance; ASTM C 297
6.21 MPa

@Temperature 21.1 °C
 900 psi

@Temperature 70.0 °F
 Flatwise Tensile; 15 Cycles, Thermal Cycling
6.27 MPa

@Temperature 21.1 °C
 910 psi

@Temperature 70.0 °F
 Flatwise Tensile; 60 Cycles, Thermal Cycling
6.55 MPa

@Temperature 21.1 °C
 950 psi

@Temperature 70.0 °F
 Flatwise Tensile; Control; Thermal Cycling
6.96 MPa

@Temperature 204 °C
 1010 psi

@Temperature 400 °F
 Flatwise Tensile; Composite Honeycomb Sandwich Performance; ASTM C 297
7.03 MPa

@Temperature 166 °C
 1020 psi

@Temperature 330 °F
 Flatwise Tensile; 60 Cycles, Thermal Cycling
7.10 MPa

@Temperature 166 °C
 1030 psi

@Temperature 330 °F
 Flatwise Tensile; 15 Cycles, Thermal Cycling
7.24 MPa

@Temperature 21.1 °C
 1050 psi

@Temperature 70.0 °F
 Flatwise Tensile; Composite Honeycomb Sandwich Performance; ASTM C 297
8.27 MPa

@Temperature 166 °C
 1200 psi

@Temperature 330 °F
 Flatwise Tensile; Control; Thermal Cycling
8.55 MPa

@Temperature 21.1 °C
 1240 psi

@Temperature 70.0 °F
 Flatwise Tensile; 1.26" Cell; Aluminum Honeycomb Sandwich Performance; ASTM C 297
Elongation at Break 2.39 %
2.39 %
Neat Resin
Tensile Modulus 3.62 GPa
525 ksi
Neat Resin
Shear Strength 17.2 MPa

@Temperature -55.0 °C
 2500 psi

@Temperature -67.0 °F
 Tensile Lap Shear; Aluminum No Primer; ASTM D1002
19.3 MPa

@Temperature 21.1 °C
 2800 psi

@Temperature 70.0 °F
 Tensile Lap Shear; Aluminum No Primer; ASTM D1002
19.3 MPa

@Temperature 21.1 °C
 2800 psi

@Temperature 70.0 °F
 Tensile Lap Shear; Composite; ASTM D1002
23.8 MPa

@Temperature -55.0 °C
 3450 psi

@Temperature -67.0 °F
 Tensile Lap Shear; Aluminum Primer HP655P; ASTM D1002
24.8 MPa

@Temperature 204 °C
 3600 psi

@Temperature 400 °F
 Tensile Lap Shear; Aluminum No Primer; ASTM D1002
24.8 MPa

@Temperature 21.1 °C
 3600 psi

@Temperature 70.0 °F
 Tensile Lap Shear; Titanium with HP655P; ASTM D1002
25.6 MPa

@Temperature 21.1 °C
 3720 psi

@Temperature 70.0 °F
 Tensile Lap Shear; Aluminum Primer HP655P; ASTM D1002
26.9 MPa

@Temperature 204 °C
 3900 psi

@Temperature 400 °F
 Tensile Lap Shear; Composite; ASTM D1002
27.6 MPa

@Temperature 204 °C
 4000 psi

@Temperature 400 °F
 Tensile Lap Shear; Aluminum Primer HP655P; ASTM D1002
27.6 MPa

@Temperature 204 °C
 4000 psi

@Temperature 400 °F
 Tensile Lap Shear; Titanium with HP655P; ASTM D1002
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 216 °C
420 °F
Wet
279 °C
535 °F
Dry
Descriptive Properties Value Comments
Areal Weight (psf) 0.04-0.12
Climbing Drum Peel (in-lb/3in) 21
350°F; Wet
25
70°F; Dry
31
70°F; Wet
Roll Width (in) 39
Standard Roll (ft2) 540