Honeywell ACLAR® 22C (5.00 mil) Copolymer Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Fluoropolymer
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Honeywell ACLAR® 22C (5.00 mil) Copolymer Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: ACLAR® 22C is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It has moisture barrier and is used for electroluminescent lamps.Information provided by Honeywell.
Physical Properties Metric English Comments
Specific Gravity 2.09 g/cc
2.09 g/cc
ASTM D1505
Density 2.08 g/cc
0.0750 lb/in³
Yield Density
Water Vapor Transmission 0.100 g/m²/day
0.00644 g/100 in²/day
100°F (37.8°C) / 100%RH; ASTM F1249
Thickness 127 microns
5.00 mil
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 150 - 250 %
150 - 250 %
ASTM D882
Film Elongation at Break, TD 150 - 250 %
150 - 250 %
ASTM D882
Secant Modulus, MD 1.241 - 1.517 GPa
180.0 - 220.0 ksi
ASTM D882
Secant Modulus, TD 1.172 - 1.379 GPa
170.0 - 200.0 ksi
ASTM D882
Tear Strength Test 300 - 350
300 - 350
graves tear TD, grams/mil; ASTM D1004
325 - 375
325 - 375
graves tear MD, grams/mil; ASTM D1004
Film Tensile Strength at Break, MD 41.4 - 55.2 MPa
6000 - 8000 psi
ASTM D882
Film Tensile Strength at Break, TD 27.6 - 41.4 MPa
4000 - 6000 psi
ASTM D882
Thermal Properties Metric English Comments
Thermal Conductivity 0.222 W/m-K
1.54 BTU-in/hr-ft²-°F
Melting Point 190 °C
374 °F
crystalline melting point; ASTM D4591
Oxygen Index 100 %
100 %
ASTM D2863
Shrinkage, MD <= 3.0 %
<= 3.0 %
300°F / 149°C - 10 min.; ASTM D1204
Shrinkage, TD <= 3.0 %
<= 3.0 %
300°F / 149°C - 10 min.; ASTM D1204
Optical Properties Metric English Comments
Haze <= 1.0 %
<= 1.0 %
ASTM D1003
Descriptive Properties Value Comments
Flammability non flammable
Users viewing this material also viewed the following: