Honeywell Aegisâ„¢ H135MP Nylon 6 Extrusion Grade Homopolymer Film

Category Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded
Manufacturer Honeywell
Trade Name Aegis™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Honeywell Aegisâ„¢ H135MP Nylon 6 Extrusion Grade Homopolymer Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Aegis H135MP is a lubricated and nucleated high viscosity, nylon 6 extrusion grade homopolymer for cast or blown film. It conforms to Food and Drug Administration requirements of 21 CFR 177.1500 as well as EU Directive 2002/72/EC. It possesses the combination of strength, toughness and thermo-forming properties associated with nylon 6 as well as excellent heat, chemical, and abrasion resistance.Applications:Processed MeatFresh Red MeatPoultryFishCheeseDried FoodChilled Fruit JuicesInformation provided by Honeywell.
Physical Properties Metric English Comments
Water Vapor Permeability 992 g mil/ (m2 day)

@Temperature 38.0 °C
64.0 g mil/ (100 in2 day)

@Temperature 100 °F
ASTM F1249
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D1505
Water Absorption 0.80 %
0.80 %
Extractable Content
1.6 %
1.6 %
in 24 hours
Moisture Absorption at Equilibrium 2.7 %
2.7 %
at 50% RH
Water Absorption at Saturation 9.5 %
9.5 %
Oxygen Transmission Rate 40.3 cc/m²/day
2.60 cc/100 in²/day
Nitrogen Transmission 14.0 cc-mm/m²-24hr-atm
35.6 cc-mil/100 in²-24hr-atm
cc/m²/day, No thickness given
Carbon Dioxide Transmission 72.8 cc-mm/m²-24hr-atm
185 cc-mil/100 in²-24hr-atm
cc/m²/day, No thickness given
Viscosity Measurement 3.75
3.75
96% Sulfuric Acid
135
135
FAV; ASTM D789
Maximum Moisture Content <= 0.080
<= 0.080
Melt Flow 1.2 g/10 min

@Load 1.00 kg,
Temperature 235 °C
1.2 g/10 min

@Load 2.20 lb,
Temperature 455 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
Molded; ASTM D882
Film Tensile Strength at Yield, MD 30.0 MPa
4350 psi
ASTM D882
Film Tensile Strength at Yield, TD 30.0 MPa
4350 psi
ASTM D882
Film Elongation at Break, MD 350 %
350 %
ASTM D882
Film Elongation at Break, TD 360 %
360 %
ASTM D882
Elongation at Break 3.7 %
3.7 %
Molded; ASTM D882
Tensile Modulus 0.610 GPa
88.5 ksi
TD; ASTM D882
0.640 GPa
92.8 ksi
MD; ASTM D882
3.13 GPa
454 ksi
Molded; ASTM D882
Flexural Strength 100 MPa
14500 psi
Molded; ASTM D790
Flexural Modulus 2.69 GPa
390 ksi
Molded; ASTM D790
Izod Impact, Notched 0.600 J/cm
1.12 ft-lb/in
Molded; ASTM D256
Tear Strength, Total 2230 N
501 lb (f)
TD, Graves; ASTM D1004
2540 N
571 lb (f)
MD, Graves; ASTM D1004
Elmendorf Tear Strength MD 85700 g
85700 g
ASTM D1922
Elmendorf Tear Strength TD 116000 g
116000 g
ASTM D1922
Film Tensile Strength at Break, MD 100 MPa
14500 psi
ASTM D882
Film Tensile Strength at Break, TD 100 MPa
14500 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ASTM D3418
Processing Properties Metric English Comments
Middle Barrel Temperature 230 - 260 °C
446 - 500 °F
Cast Film
246 - 254 °C
475 - 489 °F
Tubular (Blown) Film
Adapter Temperature 260 °C
500 °F
Tubular (Blown) Film
260 - 266 °C
500 - 511 °F
Cast Film
Die Temperature 254 °C
490 °F
Tubular (Blown) Film
260 °C
500 °F
Cast Film
Melt Temperature 240 °C
464 °F
Molded
254 - 260 °C
489 - 500 °F
Tubular (Blown) Film
260 - 270 °C
500 - 518 °F
Cast Film
Mold Temperature 80.0 °C
176 °F
Molded
Moisture Content 0.080 %
0.080 %
Descriptive Properties Value Comments
Heat Deflection Temperature, 57°C
ASTM D648
Puncture Index 480 gm/mil
ASTM D1306, MD
Puncture Strength 940 g
ASTM D1306, MD