- Honeywell Aegisâ„¢ H73ZP Nylon 6 Extrusion Grade Homopolymer Film
Honeywell Aegisâ„¢ H73ZP Nylon 6 Extrusion Grade Homopolymer Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded |
| Manufacturer | Honeywell |
| Trade Name | Aegis™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Aegisâ„¢ H73ZP Nylon 6 Extrusion Grade Homopolymer Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Aegis H73ZP is a low viscosity, nylon 6 film extrusion grade homopolymer for cast or blown film. It conforms to Food and Drug Administration requirements of 21 CFR 177.1500 as well as EU Directive 2002/72/EC. It possesses the combination of strength, toughness and thermo-forming properties associated with nylon 6 as well as excellent heat, chemical, and abrasion resistance.Applications:Processed MeatFresh Red MeatPoultryFishCheeseDried FoodChilled Fruit JuicesInformation provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Permeability | 992 g mil/ (m2 day) @Temperature 38.0 °C |
64.0 g mil/ (100 in2 day) @Temperature 100 °F |
ASTM F1249 |
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D1505 |
| Water Absorption | 1.6 % | 1.6 % | in 24 hours |
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | at 50% RH |
| Water Absorption at Saturation | 9.5 % | 9.5 % | |
| Oxygen Transmission Rate | 40.3 cc/m²/day | 2.60 cc/100 in²/day | |
| Nitrogen Transmission | 14.0 cc-mm/m²-24hr-atm | 35.6 cc-mil/100 in²-24hr-atm | cc/m²/day, No thickness given |
| Carbon Dioxide Transmission | 72.8 cc-mm/m²-24hr-atm | 185 cc-mil/100 in²-24hr-atm | cc/m²/day, No thickness given |
| Viscosity Measurement | 3.0 | 3.0 | 96% SAV |
| 73 | 73 | FAV; ASTM D789 | |
| Maximum Moisture Content | 0.080 | 0.080 | |
| Melt Flow | 4.5 g/10 min @Load 1.00 kg, Temperature 235 °C |
4.5 g/10 min @Load 2.20 lb, Temperature 455 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 78.0 MPa | 11300 psi | Molded; ASTM D882 |
| Film Tensile Strength at Yield, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Elongation at Break, MD | 339 % | 339 % | ASTM D882 |
| 359 % | 359 % | ASTM D882 | |
| Elongation at Yield | 4.2 % | 4.2 % | Molded; ASTM D882 |
| Tensile Modulus | 0.620 GPa | 89.9 ksi | TD; ASTM D882 |
| 0.710 GPa | 103 ksi | MD; ASTM D882 | |
| 2.75 GPa | 399 ksi | Molded; ASTM D882 | |
| Flexural Strength | 110 MPa | 16000 psi | Molded; ASTM D790 |
| Flexural Modulus | 2.67 GPa | 387 ksi | Molded; ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | Molded; ASTM D256 |
| Tear Strength, Total | 3290 N | 740 lb (f) | Graves, TD; ASTM D1004 |
| 3530 N | 794 lb (f) | Graves, MD; ASTM D1004 | |
| Elmendorf Tear Strength MD | 60200 g | 60200 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 54000 g | 54000 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 90.0 MPa | 13100 psi | ASTM D882 |
| 90.0 MPa | 13100 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 230 - 260 °C | 446 - 500 °F | Cast Film |
| 246 - 254 °C | 475 - 489 °F | Tubular (Blown) Film | |
| Adapter Temperature | 260 °C | 500 °F | Tubular (Blown) Film |
| 260 - 266 °C | 500 - 511 °F | Cast Film | |
| Die Temperature | 254 °C | 490 °F | Tubular (Blown) Film |
| 260 °C | 500 °F | Cast Film | |
| Melt Temperature | 240 °C | 464 °F | |
| 254 - 260 °C | 489 - 500 °F | Tubular (Blown) Film | |
| 260 - 270 °C | 500 - 518 °F | Cast Film | |
| Mold Temperature | 80.0 °C | 176 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Deflection Temperature, | 56°C | ASTM D648 |
| Puncture Index | 501 gm/mil | ASTM D1306, MD |
| Puncture Strength | 1043 g | ASTM D1306, MD |
Users viewing this material also viewed the following:
- PolyOne Edgetek® PE-10GF/000 High Density Polyethylene (HDPE), Glass Filled (discontinued **)
- Gouda Vuurvast GOLITE 95 Refractory Insulating Castable
- Saint-Gobain COHRlastic® 1010 General-Purpose Electrical-Grade Silicone Coated Fabric
- Saint-Gobain Chemfab® 10 High-Performance PTFE-Coated Glass
- ChevronTexaco Regal® 460 R&O
- Hexcel® HexWeb® CRF-3/4-ACG-.003-1.8 Chromate free ACG® Honeycomb
Copyright © lookpolymers.com All Rights Reserved