Category Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Honeywell Capran® K Coated Nylon Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Capran® K is a PVdc coated nylon 6 film designed for food packaging applications where longer shelf life is required. This film exhibits good clarity, gloss, toughness, thermoformability, and abrasion resistance. Information provided by Honeywell.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0500 lb/in³
Yield Density
Water Vapor Transmission 9.30 - 12.4 g/m²/day
0.599 - 0.799 g/100 in²/day
100°F / 100%RH); ASTM F1249
Oxygen Transmission Rate 6.20 - 14.0 cc/m²/day
0.399 - 0.902 cc/100 in²/day
77°F / 0% / RH; ASTM D3985
Thickness 25.4 microns
1.00 mil
Surface Tension >= 50 dynes/cm
>= 50 dynes/cm
Corona Treatment, uncoated side; ASTM D2578
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 37.9 - 51.0 MPa
5500 - 7400 psi
ASTM D882
Film Tensile Strength at Yield, TD 37.2 - 50.3 MPa
5400 - 7300 psi
ASTM D882
Film Elongation at Break, MD 310 - 410 %
310 - 410 %
ASTM D882
Film Elongation at Break, TD 340 - 430 %
340 - 430 %
ASTM D882
Secant Modulus, MD 0.676 - 1.207 GPa
98.0 - 175.1 ksi
ASTM D882
Secant Modulus, TD 0.724 - 1.275 GPa
105 - 184.9 ksi
ASTM D882
Coefficient of Friction 0.19 - 0.49
0.19 - 0.49
film to stainless steel; ASTM D1894
0.55 - 0.95
0.55 - 0.95
film to film; ASTM D1894
Tear Strength Test 650 - 900
650 - 900
graves tear MD, grams/mil; ASTM D1004
630 - 930
630 - 930
graves tear TD, grams/mil; ASTM D1004
Elmendorf Tear Strength, MD 0.394 - 1.97 g/micron
10.0 - 50.0 g/mil
Elmendorf Tear Strength, TD 1.57 - 3.94 g/micron
40.0 - 100 g/mil
ASTM D1922
Film Tensile Strength at Break, MD 97.9 - 141 MPa
14200 - 20500 psi
ASTM D882
Film Tensile Strength at Break, TD 82.7 - 124 MPa
12000 - 18000 psi
ASTM D882
Thermal Properties Metric English Comments
Shrinkage, MD <= 3.0 %
<= 3.0 %
300°F / 149°C - 10 minutes; ASTM D1204
Shrinkage, TD <= 3.0 %
<= 3.0 %
300°F / 149°C - 10 minutes; ASTM D1204
Optical Properties Metric English Comments
Haze <= 10 %
<= 10 %
ASTM D1003