Honeywell Halar® High Performance E-CTFE Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Fluoropolymer , ETFE/ECTFE , ECTFE Fluoropolymer
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Honeywell Halar® High Performance E-CTFE Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Halar® is a high performance Ethylene-Chlorotrifluoroethylene (E-CTFE) film with excellent mechanical, electrical and release properties. It is non-flammable, and has outstanding chemical resistance. Information provided by Honeywell.
Physical Properties Metric English Comments
Specific Gravity 1.68 g/cc
1.68 g/cc
ASTM D1505
Water Vapor Transmission 7.80 g/m²/day
0.502 g/100 in²/day
100°F (37.8°C) / 100%RH; ASTM F1249
Thickness 25.4 microns
1.00 mil
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 31.0 - 39.3 MPa
4500 - 5700 psi
ASTM D882
Film Tensile Strength at Yield, TD 27.6 - 34.5 MPa
4000 - 5000 psi
ASTM D882
Film Elongation at Break, MD 90 - 275 %
90 - 275 %
ASTM D882
Film Elongation at Break, TD 210 - 355 %
210 - 355 %
ASTM D882
Secant Modulus, MD 1.585 - 2.275 GPa
229.9 - 330.0 ksi
ASTM D882
Secant Modulus, TD 1.31 - 1.724 GPa
190 - 250.0 ksi
ASTM D882
Coefficient of Friction 0.23 - 0.33
0.23 - 0.33
film to stainless steel; ASTM D1894
0.30 - 0.86
0.30 - 0.86
film to film; ASTM D184
Tear Strength Test 400 - 570
400 - 570
graves tear MD, grams/mil; ASTM D1004
350 - 700
350 - 700
graves tear TD, grams/mil; ASTM D1004
Film Tensile Strength at Break, MD 60.7 - 107 MPa
8800 - 15500 psi
ASTM D882
Film Tensile Strength at Break, TD 42.7 - 72.4 MPa
6200 - 10500 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 240 °C
464 °F
crystalline melting point; ASTM D4591
Shrinkage, MD <= 3.0 %
<= 3.0 %
300°F / 149°C - 10 min.; ASTM D1204