Honeywell MAP-Shield™ AF Generation 2 Shrinkable Barrier Film (discontinued **)
| Category | Polymer , Film , Thermoplastic , Ethylene Vinyl Alcohol (EVOH) , Nylon |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell MAP-Shield™ AF Generation 2 Shrinkable Barrier Film
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: MAP-Shield™ AF shrinkable barrier film is ideal for modified atmosphere packaged (MAP) food products in barrier trays for extended shelf life protection. The coextruded, biaxially oriented film of nylon and EVOH, combined with metallocene PE and anti-fog materials gives you high gas barrier lidding and provides leak-proof, destruct tamper-evident seals on plastic and foam barrier food trays. Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0440 lb/in³ | Yield Density |
| Water Vapor Transmission | 14.28 g/m²/day | 0.9196 g/100 in²/day | 100°F (37.8°C) / 100%RH; ASTM F1249 |
| Oxygen Transmission Rate | <= 0.310 cc/m²/day | <= 0.0200 cc/100 in²/day | 50°F (10°C) / 80%RH; ASTM D3984 |
| <= 0.780 cc/m²/day | <= 0.0502 cc/100 in²/day | 68°F (20°C) / 65% RH; ASTM D3985 | |
| Thickness | 38.1 microns | 1.50 mil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 100 - 125 % | 100 - 125 % | ASTM D882 |
| Film Elongation at Break, TD | 85 - 100 % | 85 - 100 % | ASTM D882 |
| Tensile Modulus | 1.078 GPa | 156.3 ksi | MD; ASTM D882 |
| 1.098 GPa | 159.3 ksi | TD; ASTM D882 | |
| Coefficient of Friction | 0.38 | 0.38 | MD, film to film, side2/side2; ASTM D184 |
| 0.50 | 0.50 | MD, film to film, side1/side1; ASTM D1894 | |
| Coefficient of Friction, Static | 0.15 | 0.15 | TD, film to film, side 2/side 2; ASTM D1894 |
| 0.21 | 0.21 | TD, film to metal, side 1/metal; ASTM D1894 | |
| 0.31 | 0.31 | MD, film to metal, side 1/metal; ASTM D1894 | |
| 0.38 | 0.38 | TD, film to film, side 1/side 1; ASTM D1894 | |
| 0.40 | 0.40 | TD, film to metal, side 2/metal; ASTM D1894 | |
| 0.42 | 0.42 | TD, film to film, side 1/side 2; ASTM D1894 | |
| 0.46 | 0.46 | MD, film to metal, side 2/metal; ASTM D1894 | |
| 0.53 | 0.53 | MD, film to film, side 1/side2; ASTM D1894 | |
| Tear Strength Test | 500 | 500 | graves tear TD, grams/mil; ASTM D1004 |
| 500 | 500 | graves tear MD, grams/mil; ASTM D1004 | |
| Elmendorf Tear Strength, MD | 2.02 g/micron | 51.3 g/mil | |
| Elmendorf Tear Strength, TD | 0.5248 g/micron | 13.33 g/mil | ASTM D1922 |
| Film Tensile Strength at Break, MD | 138 MPa | 20000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 138 MPa | 20000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | -20.0 % | -20.0 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| -15.0 % | -15.0 % | 212°F / 177°C - 30 sec.; ASTM D1204 | |
| -4.00 % | -4.00 % | 140°F / 177°C - 30 sec.; ASTM D1204 | |
| Shrinkage, TD | -20.0 % | -20.0 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| -10.0 % | -10.0 % | 212°F / 177°C - 30 sec.; ASTM D1204 | |
| -1.00 % | -1.00 % | 140°F / 177°C - 30 sec.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 7.0 % | <= 7.0 % | ASTM D1003 |
| Gloss | 70 - 100 % | 70 - 100 % | at 20°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Puncture Strength | 1600 g | ASTM F1306 |