Huntsman IROGRAN® A 85 D 5001 DP TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 85 D 5001 DP TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 85 D 5001 DP is a antistatic, polyester based thermoplastic polyurethane intended for extrusion applications and injection molding. IROGRAN A 85 D 5001 DP is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable in flat die, cast die extrusion processes. IROGRAN A 85 D 5001 DP is a development material.Performance Features: Excellent wear performance Good processability Antistatic behavior Good melt flow High elasticityInformation provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | Injection molded parts; ASTM D792 |
| Melt Index of Compound | 75 g/10 min @Load 21.6 kg, Temperature 190 °C |
75 g/10 min @Load 47.6 lb, Temperature 374 °F |
MVR, [cm<sup>3</sup>/10 min] |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 85 | 85 | Injection molded parts; ASTM D2240 |
| Hardness, Shore D | 34 | 34 | Injection molded parts; ASTM D2240 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Injection molded parts; DIN 53504 |
| Elongation at Break | 620 % | 620 % | Injection molded parts; DIN 53504 |
| 100% Modulus | 0.00500 GPa | 0.725 ksi | Injection molded parts; DIN 53504 |
| 300% Modulus | 0.0110 GPa | 1.60 ksi | Injection molded parts; DIN 53504 |
| Rebound | 36 % | 36 % | Bayshore, Injection molded parts; ASTM D2632 |
| Tear Strength | 105 kN/m | 600 pli | Injection molded parts; ASTM D624 |
| Abrasion | 25 | 25 | mm<sup>3</sup>, Injection molded; DIN 53516 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+8 ohm | 1.00e+8 ohm | Injection molded parts |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| 25.0 - 45.0 °C | 77.0 - 113 °F | Injection | |
| Middle Barrel Temperature | 180 - 205 °C | 356 - 401 °F | Extrusion |
| Nozzle Temperature | 185 - 205 °C | 365 - 401 °F | Extrusion |
| 185 - 210 °C | 365 - 410 °F | Injection | |
| Adapter Temperature | 180 - 205 °C | 356 - 401 °F | Extrusion |
| Die Temperature | 185 - 205 °C | 365 - 401 °F | Extrusion |
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 190-210°C | Injection |
Users viewing this material also viewed the following:
- PTS Tristar® PC-06R 6.0 MFI Grade Polycarbonate, With Release
- Inno-Comp INNOBATCH® PPH 6260 60% Chalk Filled Polypropylene Homopolymer
- Seals Eastern 7202 Nitrile Rubber
- Borealis Borstar® ME3440 Black Medium Density Polyethylene for Pressure Pipes
- Vyncolit G865 Novolac Phenolic
- Fainplast Compounds GS 650 Flexible PVC, Injection Molding for Footwear
- A. Schulman ComAlloy E-16903B Nylon 6/6, Electrically Conductive - Stainless Steel Fiber Filled
- Asahi Kasei Thermylene® P6-20FG-0738 20% Glass Fiber Reinforced, High Impact
- BASF Ultradur® B 4300 K6 30% Glass Bead Filled PBT
- DuPont Performance Polymers Hypalon® 30 Chlorosulfonated Polyethylene Rubber, Gum Compound (discontinued **)&
Copyright © lookpolymers.com All Rights Reserved