Huntsman IROGRAN® A 86 E 4486 Polyester-Based TPU-Injection Extrusion Grade
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 86 E 4486 Polyester-Based TPU-Injection Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 86 E 4486 is a thermoplastic polyester- polyurethane for injection molding and extrusion applications. Additional characteristics of the product are excellent mechanical properties and high tear strength.Performance Features: Good melt flow High production rates High wear resistance Dynamically highly loadable Halogen-free UL 94 Classification V2 Applications: For the production of spiral hoses, hose jackets for high pressure hoses, vacuum cleaner hoses, profiles.Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | ASTM D995 |
| Melt Index of Compound | 75 g/10 min @Load 21.6 kg, Temperature 190 °C |
75 g/10 min @Load 47.6 lb, Temperature 374 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 84 | 84 | ASTM D2240 |
| Hardness, Shore D | 33 | 33 | ASTM D2240 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | DIN 53504 |
| Elongation at Break | 700 % | 700 % | ASTM D412 |
| 100% Modulus | 0.00520 GPa | 0.754 ksi | DIN 53504 |
| 300% Modulus | 0.0104 GPa | 1.51 ksi | DIN 53504 |
| Rebound | 40 % | 40 % | Bayshore; ASTM D2632 |
| Tear Strength | 96.4 kN/m | 550 pli | ASTM D624 |
| Abrasion | 25 | 25 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 21 % @Temperature 23.0 °C, Time 252000 sec |
21 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 35 % @Temperature 70.0 °C, Time 86400 sec |
35 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 155 - 173 °C | 311 - 343 °F | Huntsman/TMA |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |
Users viewing this material also viewed the following:
- Zircar Zirconia Buster M-15 Alumina Boards, Discs & Cylinders Insulation
- LG Chemical R120 EPS, Flame Retardant
- Shakespeare CL-10XT Super Tough Nylon Copolymer Fishing Line, 12 lb
- Borealis FA3220 Low Density Polyethylene
- EMS-Grivory Grivory® 2S 20 nat PA610
- Ensinger Tecapeek® XP-117 Compression Molded PEEK Compound, 25% PTFE Filled
- ExxonMobil Escorene® LL-3201 LLDPE/Hexene Premium High Strength 0.6 mil Film, Stiff (discontinued **)
- Solvay Specialty Polymers Diofan® A 036 Polyvinylidene Chloride (PVDC) (discontinued **)
- Solvay Specialty Polymers Amodel® AS-4133 HN Polyphthalamide (PPA), Dry, 33% Glass Fiber Reinforcement, Heat Stabilizer
Copyright © lookpolymers.com All Rights Reserved