Huntsman IROGRAN® A 92 K 5031 TPU-High Temperature Performance
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 92 K 5031 TPU-High Temperature Performance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycaprolactone and ether based. Good processability and compression set. Excellent resistance to high temperatures, water, grease, and oils.. Used in seals, wheels, and rollers.Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 92 | 92 | ASTM D2240 |
| Hardness, Shore D | 46 | 46 | ASTM D2240 |
| Tensile Strength at Break | 54.0 MPa | 7830 psi | DIN 53504 |
| Elongation at Break | 580 % | 580 % | ASTM D412 |
| 100% Modulus | 0.0114 GPa | 1.65 ksi | DIN 53504 |
| 300% Modulus | 0.0180 GPa | 2.61 ksi | DIN 53504 |
| Rebound | 41 % | 41 % | Bayshore; ASTM D2632 |
| Tear Strength | 130 kN/m | 740 pli | ASTM D624 |
| Abrasion | 20 | 20 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 14 % @Temperature 23.0 °C, Time 252000 sec |
14 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 26 % @Temperature 70.0 °C, Time 86400 sec |
26 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 180 - 195 °C | 356 - 383 °F | Huntsman/TMA |