Huntsman IROGRAN® PS455-200 TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® PS455-200 TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN PS455-200 is a polyester based thermoplastic polyurethane intended for extrusion applications. IROGRAN PS455-200 is part of the HUNTSMAN film and sheet product range and offers a specially designed, flexible material with a broad processing window particularly suitable for film and sheet, textile laminations, and compounding. Performance Features: FDA grade (21 CFR 175.105, 177.2600) Soft High elongation Tough Good low temperature properties Wide processing windowApplications: Textile lamination Compounding Information provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | Injection molded parts; ASTM D792 |
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 177 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 351 °F |
MVR, [cm<sup>3</sup>/10 min] |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 78 | 78 | Injection molded parts; ASTM D2240 |
| Tensile Strength at Break | 42.0 MPa | 6090 psi | 0.025" extruded film; DIN 53504 |
| Elongation at Break | 700 % | 700 % | 0.025" extruded film; DIN 53504 |
| 100% Modulus | 0.00200 GPa | 0.290 ksi | 0.025" extruded film; DIN 53504 |
| 300% Modulus | 0.00500 GPa | 0.725 ksi | 0.025" extruded film; DIN 53504 |
| Rebound | 50 % | 50 % | Bayshore; ASTM D2632 |
| Tear Strength | 66.6 kN/m | 380 pli | 0.025" extruded film; ASTM D624 |
| Abrasion | 50 | 50 | mm<sup>3</sup>, Injection molded; DIN 53516 |
| Compression Set | 40 % @Temperature 22.8 °C, Time 252000 sec |
40 % @Temperature 73.0 °F, Time 70.0 hour |
Injection molded; ASTM D395 |
| 90 % @Temperature 70.0 °C, Time 86400 sec |
90 % @Temperature 158 °F, Time 24.0 hour |
Injection molded; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 110 - 130 °C | 230 - 266 °F | 0.025" extruded film, |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 140 °C | 284 °F | Extrusion |
| Middle Barrel Temperature | 150 °C | 302 °F | Extrusion |
| Adapter Temperature | 150 °C | 302 °F | Extrusion |
| Die Temperature | 150 °C | 302 °F | Extrusion |
Users viewing this material also viewed the following:
- PolyOne reFlex™ 300 Plasticizer, Bio-derived
- PolyOne Dynalloy™ OBC 8100-N75 Thermoplastic Elastomer (TPE)
- STAR Thermoplastic Alloys & Rubbers StarTUFF TF 40-HR-9 TPE
- SABIC Innovative Plastics NORYL FXN119BK PPE+HIPS (Europe-Africa-Middle East)
- Unitika A175G15 PA66, 15% Glass Fiber Reinforced, Dry
- Colorite Polymers 87-638A General Purpose Vinyl Compound
- Adell BH-38 Nylon 6, 40% Mineral Filled
- Arlon 44576R016 0.016" (0.406 mm) Cured/Uncured Silicone Rubber with Fiberglass Substrate
- 3M Dyneon™ TFM™ X 1630 PTFE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved