Huntsman PE5032 Extrusion Coating Polyethylene  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman PE5032 Extrusion Coating Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Homopolymer and FDA compliant.Features: Excellent draw down, low neck-in, excellent heat sealability, good adhesion, low smoking, no edge weave, and excellent printability.Applications: Extrusion: coating grade, milk cartons, military barrier, and general coating.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under condition of use B through H described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.923 g/cc
0.0333 lb/in³
ASTM D1505
Melt Flow 4.5 g/10 min
4.5 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 52
52
ASTM D2240
Tensile Strength, Ultimate 10.0 MPa
1450 psi
ASTM D638
Tensile Strength, Yield 12.0 MPa
1740 psi
ASTM D638
Film Elongation at Break, MD 250 %
250 %
ASTM D882
Film Elongation at Break, TD 380 %
380 %
ASTM D882
Elongation at Break 400 %
400 %
ASTM D638
Modulus of Elasticity 0.290 GPa
42.1 ksi
Secant; ASTM D638
Secant Modulus, MD 0.180 GPa
26.1 ksi
ASTM D882
Secant Modulus, TD 0.220 GPa
31.9 ksi
ASTM D882
Film Tensile Strength at Break, MD 17.0 MPa
2470 psi
ASTM D882
Film Tensile Strength at Break, TD 14.0 MPa
2030 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 93.0 °C
199 °F
ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 249 - 288 °C
480 - 550 °F