Huntsman Rexell® V8402 Cast Film Extrusion LLDPE  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman Rexell® V8402 Cast Film Extrusion LLDPE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultra linear-low density copolymer, blown film extrusion, FDA compliant.Features: Excellent mechanical strength, low sealing temperature, and good flex crack resistanceApplications: Sealing layer in coextruded filmsFilm properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.910 g/cc
0.0329 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 2.2 g/10 min
2.2 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 690 %
690 %
ASTM D882
Film Elongation at Break, TD >= 700 %
>= 700 %
ASTM D882
Secant Modulus, MD 0.117 GPa
17.0 ksi
ASTM D882
Secant Modulus, TD 0.138 GPa
20.0 ksi
ASTM D882
Elmendorf Tear Strength MD 470 g
470 g
ASTM D1922
Elmendorf Tear Strength TD 680 g
680 g
ASTM D1922
Elmendorf Tear Strength, MD 18.5 g/micron
470 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 26.8 g/micron
680 g/mil
ASTM D1922
Dart Drop 8.98 g/micron
228 g/mil
ASTM D1709
Dart Drop Test 228 g
0.503 lb
ASTM D1709
Film Tensile Strength at Break, MD 32.0 MPa
4640 psi
ASTM D882
Film Tensile Strength at Break, TD >= 15.0 MPa
>= 2180 psi
ASTM D882
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D1003
Gloss 70 %
70 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 175 - 215 °C
347 - 419 °F