- ITW Devcon Metal Repair Wear Resistant Epoxy (WR-2), Dark Grey
ITW Devcon Metal Repair Wear Resistant Epoxy (WR-2), Dark Grey
| Category | Polymer , Adhesive , Thermoset |
| Manufacturer | ITW Devcon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ITW Devcon Metal Repair Wear Resistant Epoxy (WR-2), Dark Grey.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by ITW Devcon
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.99 g/cc | 0.0719 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | Cured; ASTM D2240 |
| Tensile Strength at Break | 29.6 MPa | 4300 psi | ASTM D638 |
| Modulus of Elasticity | 5.17 GPa | 750 ksi | ASTM D638 |
| Flexural Strength | 44.8 MPa | 6500 psi | ASTM D790 |
| Compressive Strength | 67.6 MPa | 9800 psi | ASTM D695 |
| Adhesive Bond Strength | 15.2 MPa | 2200 psi | tensile shear; ASTM D1002 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 57.6 µm/m-°C @Temperature 20.0 °C |
32.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.699 W/m-K | 4.84 BTU-in/hr-ft²-°F | ASTM C177 |
| Maximum Service Temperature, Air | 121 °C | 250 °F | dry |
| Shrinkage | 0.050 % | 0.050 % | Cured; ASTM D2566 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 6.3 @Frequency 1000 Hz |
6.3 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 960 min | 16.0 hour | Functional cure |
| Pot Life | 60.0 min @Temperature 23.9 °C |
60.0 min @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Coverage per pound, in² @ 1/4" thickness | 56 | |
| Mix ratio (Resin:Hardener) | 9:1 | |
| Mix ratio by volume (Resin:Hardener) | 4:1 |
Users viewing this material also viewed the following:
- Plenco 7300 Phenolic, Nodular, Transfer Molded (discontinued **)
- Star Plastics PC1510R Molding Grade PC
- Techmer ES Electrablend® ABS CF15 FR BK 15% Carbon Filled
- Polyplastics Duracon® TR-20 Acetal Co-polymer (POM), Mineral filling, Mineral filling, High rigidity, Low warpage
- A. Schulman POLYBATCH™ White LL8844 GP
- E-Polymers Tekaloy® T80GFR , Flame Retardant, 30% Glass Fiber Reinforced PBT/ABS Alloy
- Braskem Evateno® 3019 PE EVA Foam Copolymer
- BASF Ultradur B 4040 G6 LS High Speed BK15029 30% Glass Filled PBT/PET
- 3M Scotch-Weld™ DP8405NS Acrylic Adhesives
- Eastman Tenite Butyrate 581A3720016 Clear, Trsp Cellulose Acetate Butyrate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved