Industrial Laminates/Norplex NP180 Synthetic Fabric  (discontinued **)

Category Polymer , Thermoset , Aramid
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP180 Synthetic Fabric  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: aramid fabric material with a high performance epoxy resin matrix. Excellent electrical and mechanical properties at elevated temperatures and in adverse environments.Thickness Tested: 0.062", 0.125", and 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
Moisture Absorption at Equilibrium 0.31 %

@Thickness 1.57 mm
0.31 %

@Thickness 0.0620 in
Mechanical Properties Metric English Comments
Hardness, Rockwell M 80 - 100

@Thickness 1.57 mm
80 - 100

@Thickness 0.0620 in
Tensile Strength, Yield 400 MPa

@Thickness 3.17 mm
58000 psi

@Thickness 0.125 in
CW
427 MPa

@Thickness 3.17 mm
62000 psi

@Thickness 0.125 in
LW
Flexural Strength 386 MPa

@Thickness 1.57 mm
56000 psi

@Thickness 0.0620 in
CW
386 MPa

@Thickness 1.57 mm
56000 psi

@Thickness 0.0620 in
LW
Compressive Strength 545 MPa

@Thickness 12.7 mm
79000 psi

@Thickness 0.500 in
Flatwise
Izod Impact, Unnotched 4.27 J/cm

@Thickness 12.7 mm
8.00 ft-lb/in

@Thickness 0.500 in
CW, E-48/50
5.82 J/cm

@Thickness 12.7 mm
10.9 ft-lb/in

@Thickness 0.500 in
LW, E-48/50
Thermal Properties Metric English Comments
CTE, linear 36.3 µm/m-°C

@Thickness 1.57 mm,
Temperature 40.0 - 105 °C
20.2 µin/in-°F

@Thickness 0.0620 in,
Temperature 104 - 221 °F
x-axis
262 µm/m-°C

@Thickness 1.57 mm,
Temperature 105 - 155 °C
146 µin/in-°F

@Thickness 0.0620 in,
Temperature 221 - 311 °F
x-axis
Maximum Service Temperature, Air 180 °C
356 °F
Maximum Operating Temperature
Glass Transition Temp, Tg 145 °C
293 °F
Tg
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Dielectric Constant 3.91

@Thickness 1.57 mm
3.91

@Thickness 0.0620 in
Permittivity, Cond D-24/23
Dielectric Strength 19.7 kV/mm

@Thickness 1.57 mm
500 kV/in

@Thickness 0.0620 in
D-48/50
25.6 kV/mm

@Thickness 1.57 mm
650 kV/in

@Thickness 0.0620 in
Condition - A
Dielectric Breakdown 47000 V

@Thickness 1.57 mm
47000 V

@Thickness 0.0620 in
Condition A
54000 V

@Thickness 1.57 mm
54000 V

@Thickness 0.0620 in
D-48/50
Dissipation Factor 0.0275

@Thickness 1.57 mm
0.0275

@Thickness 0.0620 in
Cond D-24/23
Arc Resistance 121 sec

@Thickness 3.17 mm
121 sec

@Thickness 0.125 in
ASTM D495