Material Notes:
Description: 17 oz. aramid and "soft glass" fibers are combined to make a fabric that is stronger than pure aramid and less abrasive than glass fabrics. This material is impregnated with a high temperature epoxy resin matrix, which produces a composite with excellent mechanical strength at elevated temperatures and adverse environments. Applications include wear plates for conveyor systems, valve plates, and compressor and pump vanes.Thickness Tested: 0.125", 0.250" & 0.500"
Physical Properties Metric English Comments
Moisture Absorption at Equilibrium 0.50 %

@Thickness 1.57 mm
 0.50 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Tensile Strength, Yield 179 MPa

@Thickness 1.57 mm
 26000 psi

@Thickness 0.0620 in
 CW; ASTM D638
200 MPa

@Thickness 1.57 mm
 29000 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 11.7 GPa

@Thickness 1.57 mm
 1700 ksi

@Thickness 0.0620 in
 CW; ASTM D229
12.4 GPa

@Thickness 1.57 mm
 1800 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 138 MPa

@Thickness 1.57 mm
 20000 psi

@Thickness 0.0620 in
 CW; ASTM D790
324 MPa

@Thickness 1.57 mm
 47000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 221 MPa

@Thickness 12.7 mm
 32000 psi

@Thickness 0.500 in
 ASTM D695
Izod Impact, Unnotched 2.14 J/cm

@Thickness 12.7 mm
 4.00 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
8.01 J/cm

@Thickness 12.7 mm
 15.0 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 44.4 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 24.7 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 26.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 14.4 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Constant 4.3

@Thickness 1.57 mm
 4.3

@Thickness 0.0620 in
 Permittivity, Cond D-24/23; ASTM D150
Dielectric Breakdown 45000 V

@Thickness 1.57 mm
 45000 V

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S/S
46000 V

@Thickness 1.57 mm
 46000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Dissipation Factor 0.021

@Thickness 1.57 mm
 0.021

@Thickness 0.0620 in
 Cond D-24/23; ASTM D150
Descriptive Properties Value Comments
Bond Strength 2400 lb
0.5", ASTM D229
Color Natural