Industrial Laminates/Norplex NP555 Carbon Fiber  (discontinued **)

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Phenolic
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP555 Carbon Fiber  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: NP555 is composed of carbon fiber fabric and a phenolic resin system. It has excellent moisture resistance and physical properties. This material was designed to replace asbestos vane material for large, high performance compressors.Thickness Tested: 0.062", 0.125" and 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.50 - 1.60 g/cc

@Thickness 1.57 mm
1.50 - 1.60 g/cc

@Thickness 0.0620 in
ASTM D792
Moisture Absorption at Equilibrium 0.10 %

@Thickness 1.57 mm
0.10 %

@Thickness 0.0620 in
ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 95 - 115

@Thickness 1.57 mm
95 - 115

@Thickness 0.0620 in
ASTM D785
Tensile Strength, Yield 379 MPa

@Thickness 1.57 mm
55000 psi

@Thickness 0.0620 in
CW; ASTM D638
552 MPa

@Thickness 1.57 mm
80000 psi

@Thickness 0.0620 in
LW; ASTM D638
Modulus of Elasticity 8.27 GPa

@Thickness 1.57 mm
1200 ksi

@Thickness 0.0620 in
CW; ASTM D229
8.96 GPa

@Thickness 1.57 mm
1300 ksi

@Thickness 0.0620 in
LW; ASTM D229
Flexural Strength 323 MPa

@Thickness 1.57 mm
46800 psi

@Thickness 0.0620 in
CW; ASTM D790
381 MPa

@Thickness 1.57 mm
55200 psi

@Thickness 0.0620 in
LW; ASTM D790
Izod Impact, Unnotched 19.8 J/cm

@Thickness 12.7 mm
37.0 ft-lb/in

@Thickness 0.500 in
CW, Cond E-48/50; ASTM D256
21.4 J/cm

@Thickness 12.7 mm
40.0 ft-lb/in

@Thickness 0.500 in
LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 6.00 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
3.33 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 11.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
6.11 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 230 °C
446 °F
Flammability, UL94 HB

@Thickness 1.57 mm
HB

@Thickness 0.0620 in
Descriptive Properties Value Comments
Bond Strength 600 lb
0.5", ASTM D229
Color Black