Industrial Laminates/Norplex NP610 Paper Base Laminate

Category Polymer , Thermoset , Phenolic
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP610 Paper Base Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Phenolic paper based grade for mechanical applications. Good tensile, compressive and flexural strength. Primarily a machining material, but may be hot punched up to .093" thick.Thickness Tested: 0.062", 0.125", and 0.500".
Physical Properties Metric English Comments
Specific Gravity 1.35 - 1.45 g/cc

@Thickness 1.57 mm
1.35 - 1.45 g/cc

@Thickness 0.0620 in
ASTM D792
Moisture Absorption at Equilibrium 1.8 %

@Thickness 1.57 mm
1.8 %

@Thickness 0.0620 in
ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 95 - 115

@Thickness 1.57 mm
95 - 115

@Thickness 0.0620 in
ASTM D785
Tensile Strength, Yield 110 MPa

@Thickness 1.57 mm
16000 psi

@Thickness 0.0620 in
CW; ASTM D638
138 MPa

@Thickness 1.57 mm
20000 psi

@Thickness 0.0620 in
LW; ASTM D638
Modulus of Elasticity 9.65 GPa

@Thickness 1.57 mm
1400 ksi

@Thickness 0.0620 in
CW; ASTM D229
13.1 GPa

@Thickness 1.57 mm
1900 ksi

@Thickness 0.0620 in
LW; ASTM D229
Flexural Strength 193 MPa

@Thickness 1.57 mm
28000 psi

@Thickness 0.0620 in
CW; ASTM D790
234 MPa

@Thickness 1.57 mm
34000 psi

@Thickness 0.0620 in
LW; ASTM D790
Compressive Strength 241 MPa

@Thickness 12.7 mm
35000 psi

@Thickness 0.500 in
ASTM D695
Shear Strength 103 MPa

@Thickness 15.7 mm
15000 psi

@Thickness 0.620 in
ASTM D732
Izod Impact, Unnotched 0.406 J/cm

@Thickness 12.7 mm
0.760 ft-lb/in

@Thickness 0.500 in
CW, Cond E-48/50; ASTM D256
0.438 J/cm

@Thickness 12.7 mm
0.820 ft-lb/in

@Thickness 0.500 in
LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 13.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
7.22 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 17.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
9.44 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 130 °C
266 °F
Flammability, UL94 HB

@Thickness 1.57 mm
HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Strength 23.6 kV/mm

@Thickness 1.57 mm
600 kV/in

@Thickness 0.0620 in
Cond A; ASTM D229 S.T.
Dielectric Breakdown 40000 V

@Thickness 1.57 mm
40000 V

@Thickness 0.0620 in
Cond A; ASTM D229 S/S
Arc Resistance 90 sec

@Thickness 3.17 mm
90 sec

@Thickness 0.125 in
ASTM D495
Descriptive Properties Value Comments
Bond Strength 1000 lb
0.5", ASTM D229
Color Natural, Black, Chocolate