Ineos ABS Centrex® 825 ASA+AES Blend  (discontinued **)

Category Polymer , Thermoplastic , AES Polymer , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Centrex® 825 ASA+AES Blend  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Key Features:UnfilledHigh impact or high impact modifiedLight stabilized or stable to lightU.V. stabilized or stable to weatherSuitable processing methods:Profile extrusionSheet extrusionThermoformingInformation provided by Bayer Polymers.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired 100% of Ineos ABS.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
Melt Flow 8.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
8.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
cm³/10 min.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 36.7 MPa
5320 psi
Elongation at Break 50 %
50 %
Nominal
Elongation at Yield 3.0 %
3.0 %
Tensile Modulus 1.70 GPa
247 ksi
Charpy Impact, Notched 3.25 J/cm²
15.5 ft-lb/in²
0.290 J/cm²

@Temperature -30.0 °C
1.38 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 99.0 µm/m-°C

@Temperature 20.0 °C
55.0 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C
198 °F
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
Vicat Softening Point 94.0 °C
201 °F
50°C/h 50N
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL Recognized
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
UL Recognized
Electrical Properties Metric English Comments
Dissipation Factor 0.0119

@Frequency 1e+6 Hz
0.0119

@Frequency 1e+6 Hz
0.0244

@Frequency 100 Hz
0.0244

@Frequency 100 Hz
Processing Properties Metric English Comments
Melt Temperature 250 °C
482 °F
Injection Molding
Mold Temperature 60.0 °C
140 °F
Injection Molding
Injection Velocity 200 mm/sec
7.87 in/sec
Injection Pressure 60.0 MPa
8700 psi