Ineos ABS Lustran® 1148 General Purpose, High-Impact  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® 1148 General Purpose, High-Impact  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Bayer Corporation, Plastics DivisionLANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired 100% of Ineos ABS. This product is no longer listed as a standard NAFTA product.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
ASTM D955
Melt Flow 1.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
1.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100
100
Tensile Strength, Yield 37.0 MPa
5370 psi
ASTM D638
Tensile Modulus 2.30 GPa
334 ksi
ASTM D638
Flexural Yield Strength 64.8 MPa
9400 psi
ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
ASTM D790
Izod Impact, Notched 4.80 J/cm

@Thickness 3.17 mm
8.99 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 92.0 µm/m-°C

@Temperature 20.0 °C
51.1 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C

@Thickness 12.7 mm
189 °F

@Thickness 0.500 in
Unannealed; ASTM D648
Vicat Softening Point 106 °C
223 °F
Rate B; ASTM D1525
UL RTI, Electrical 60.0 °C

@Thickness 1.60 mm
140 °F

@Thickness 0.0630 in
UL746B
UL RTI, Mechanical with Impact 60.0 °C

@Thickness 1.60 mm
140 °F

@Thickness 0.0630 in
UL746B
UL RTI, Mechanical without Impact 60.0 °C

@Thickness 1.60 mm
140 °F

@Thickness 0.0630 in
UL746B
Flammability, UL94 HB

@Thickness 1.57 mm
HB

@Thickness 0.0618 in
HB

@Thickness 1.57 mm
HB

@Thickness 0.0618 in
Optical Properties Metric English Comments
Transmission, Visible 0.00 %
0.00 %
Opaque only