Ineos ABS Lustran® Guardian™ 682 ABS, Injection Molding Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Ineos ABS
Trade Name Lustran® Guardian™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® Guardian™ 682 ABS, Injection Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lustran® ABS 682 is a high performance, HCFC-141b resistant grade of ABS for injection molded refrigerator and freezer components.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM-D792, ISO 1183
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM-D955
Melt Flow 0.70 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 0.70 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM-D1238, ISO 1133
5.2 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 5.2 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM-D1238, ISO 1133
8.0 g/10 min

@Load 10.0 kg,
Temperature 230 °C
 8.0 g/10 min

@Load 22.0 lb,
Temperature 446 °F
 ASTM-D1238, ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 32.0 MPa
4640 psi
ASTM-D638
34.0 MPa

@Temperature 23.0 °C
 4930 psi

@Temperature 73.4 °F
 50-mm/min; ISO 527
52.0 MPa

@Temperature -18.0 °C
 7540 psi

@Temperature -0.400 °F
 50-mm/min; ISO 527
Tensile Strength, Yield 43.0 MPa
6240 psi
ASTM-D638
48.0 MPa

@Temperature 23.0 °C
 6960 psi

@Temperature 73.4 °F
 50-mm/min; ISO 527
64.0 MPa

@Temperature -18.0 °C
 9280 psi

@Temperature -0.400 °F
 50-mm/min; ISO 527
Elongation at Break 34 %
34 %
ASTM-D638
15 %

@Temperature -18.0 °C
 15 %

@Temperature -0.400 °F
 50-mm/min; ISO 527
20 %

@Temperature 23.0 °C
 20 %

@Temperature 73.4 °F
 50-mm/min; ISO 527
Tensile Modulus 2.47 GPa
358 ksi
ASTM-D638
2.42 GPa

@Temperature 23.0 °C
 351 ksi

@Temperature 73.4 °F
 1-mm/min; ISO 527
2.81 GPa

@Temperature -18.0 °C
 408 ksi

@Temperature -0.400 °F
 1-mm/min; ISO 527
Flexural Yield Strength 72.0 MPa
10400 psi
ASTM-D790
72.0 MPa
10400 psi
ISO 178
Flexural Modulus 2.48 GPa
360 ksi
ISO 178
2.53 GPa
367 ksi
ASTM-D790
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature -18.0 °C
 5.71 ft-lb/in²

@Temperature -0.400 °F
 10.0-mm x 4.0-mm, 0.25-mm notch; ISO 180
13.8 kJ/m²

@Temperature -18.0 °C
 6.57 ft-lb/in²

@Temperature -0.400 °F
 12.7-mm x 3.2-mm, 0.25-mm notch; ASTM-D256
29.0 kJ/m²

@Temperature 23.0 °C
 13.8 ft-lb/in²

@Temperature 73.4 °F
 10.0-mm x 4.0-mm, 0.25-mm notch; ISO 180
48.0 kJ/m²

@Temperature 23.0 °C
 22.8 ft-lb/in²

@Temperature 73.4 °F
 12.7-mm x 3.2-mm, 0.25-mm notch; ASTM-D256
Impact Test 20.0 J

@Temperature 23.0 °C
 14.8 ft-lb

@Temperature 73.4 °F
 Multiaxial Impact (3.4 m/s, 40-mm ring, M831 Striker); Energy to Peak Load; ASTM-D3763
26.0 J

@Temperature -18.0 °C
 19.2 ft-lb

@Temperature -0.400 °F
 Multiaxial Impact (3.4 m/s, 40-mm ring, M831 Striker); Energy to Peak Load; ASTM-D3763
30.0 J

@Temperature -18.0 °C
 22.1 ft-lb

@Temperature -0.400 °F
 Multiaxial Impact (3.4 m/s, 40-mm ring, M831 Striker); Total Energy; ASTM-D3763
33.0 J

@Temperature 23.0 °C
 24.3 ft-lb

@Temperature 73.4 °F
 Multiaxial Impact (3.4 m/s, 40-mm ring, M831 Striker); Total Energy; ASTM-D3763
Thermal Properties Metric English Comments
CTE, linear 102 µm/m-°C
56.7 µin/in-°F
ASTM-D696
Deflection Temperature at 1.8 MPa (264 psi) 94.5 °C
202 °F
Annealed (2 hours at 80°C); ISO 75
95.1 °C
203 °F
Annealed (2 hours at 80°C); ASTM-D648
Vicat Softening Point 94.1 °C

@Load 5.00 kg
 201 °F

@Load 11.0 lb
 50°C/hour; ISO 306
97.0 °C

@Load 5.00 kg
 207 °F

@Load 11.0 lb
 120°C/hour; ISO 306
108.9 °C

@Load 1.00 kg
 228.0 °F

@Load 2.20 lb
 120°C/hour; ASTM-D1525
Flammability, UL94 HB

@Thickness 1.10 mm
 HB

@Thickness 0.0433 in
 White
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 All Colors
Optical Properties Metric English Comments
Gloss 87 %
87 %
Angle 20°; Gardner
96 %
96 %
Angle 60°; Gardner