- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Ineos ABS Lustran® H950
Ineos ABS Lustran® H950
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® H950.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Very high heat resistance,,Property data per ISO test methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
Estimated using room temperature density |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | |
| Elongation at Yield | 2.9 % | 2.9 % | |
| Tensile Modulus | 2.60 GPa | 377 ksi | |
| Charpy Impact Unnotched | 14.0 J/cm² | 66.6 ft-lb/in² | |
| 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 0.700 µm/m-°C @Temperature 20.0 °C |
0.389 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | |
| Vicat Softening Point | 113 °C | 235 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
|
| 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
||
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | |
| Dissipation Factor | 0.0060 @Frequency 100 Hz |
0.0060 @Frequency 100 Hz |
|
| 0.010 @Frequency 1e+6 Hz |
0.010 @Frequency 1e+6 Hz |
Users viewing this material also viewed the following:
- Nabaltec APYRAL® 22 Al(OH)3
- Polycasa CAST PMMA
- PSM Industries Pacific Sintered Metals Nickel Steel FN-255-S(HT) Powdered Metal
- I. Stern 1335 Prime Homopolymer Polypropylene
- Solvay TECHNYL® A 218HP V30 Black 21N PA66, 30% glass fiber, DRY
- SABIC Innovative Plastics ULTEM 2100R PEI
- SABIC Innovative Plastics LNP THERMOCOMP DFZ22P PC (Asia Pacific)
- A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound
- PlastxWorld Veroplas PA2002MI Nylon 6
- UBE UBESTA® 3030U Nylon 12 (After Isopropanol for 500 hours)
Copyright © lookpolymers.com All Rights Reserved