Ineos ABS NOVODUR® P2L-AT ABS, Injection Grade  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS NOVODUR® P2L-AT ABS, Injection Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Injection molding grade, very easy flow, antistatic, high stiffness, high gloss.Applications: Telephones, household goods, disk and video housings, office equipment.Information provided by the manufacturer.Novodur is produced by Styrolution (2014). This grade was discontinued prior to Styrolution's acquisition of the Novodur product line.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
Water Absorption 0.30 %
0.30 %
Saturation in water
Water Absorption at Saturation 0.30 %
0.30 %
Melt Flow 45 g/10 min

@Load 10.0 kg,
Temperature 220 °C
45 g/10 min

@Load 22.0 lb,
Temperature 428 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 45.0 MPa
6530 psi
Elongation at Yield 2.1 %
2.1 %
Tensile Modulus 2.70 GPa
392 ksi
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
0.350 J/cm²

@Temperature -30.0 °C
1.67 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 96.0 °C
205 °F
Deflection Temperature at 1.8 MPa (264 psi) 92.0 °C
198 °F
Vicat Softening Point 96.0 °C
205 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
Dielectric Constant 3.0

@Frequency 1e+6 Hz
3.0

@Frequency 1e+6 Hz
3.1

@Frequency 100 Hz
3.1

@Frequency 100 Hz
Dielectric Strength 31.0 kV/mm
787 kV/in
Dissipation Factor 0.0080

@Frequency 100 Hz
0.0080

@Frequency 100 Hz
0.0080

@Frequency 1e+6 Hz
0.0080

@Frequency 1e+6 Hz
Comparative Tracking Index 600 V
600 V