Ineos Nova 5404 High Impact Polystyrene

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer Ineos Nova
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos Nova 5404 High Impact Polystyrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High impact, Good environmental stress crack resistance, USP Class VIApplications: Thermoformed containers and lids, Hot and cold beverage cups, Custom sheet, Single service packagingProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.Information provided by NOVA Chemicals.INEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets. 
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955
Melt Flow 2.5 g/10 min
2.5 g/10 min
Condition G
Mechanical Properties Metric English Comments
Hardness, Rockwell M 40
40
Tensile Strength, Yield 20.0 MPa
2900 psi
ASTM D638
Elongation at Break 70 %
70 %
ASTM D638
Modulus of Elasticity 1.897 GPa
275.1 ksi
ASTM D638
Flexural Yield Strength 48.0 MPa
6960 psi
ASTM D790
Flexural Modulus 2.069 GPa
300.1 ksi
ASTM D790
Izod Impact, Notched 1.12 J/cm

@Diameter 3.17 mm
2.10 ft-lb/in

@Diameter 0.125 in
bar, 0.010" notch radius; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 75.0 µm/m-°C

@Temperature 20.0 °C
41.7 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
183 °F
ASTM D648
Vicat Softening Point 99.0 °C
210 °F
ASTM D1525
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Dielectric Constant 2.51

@Frequency 1e+6 Hz
2.51

@Frequency 1e+6 Hz
Dielectric Strength 15.7 kV/mm

@Thickness 3.17 mm
400 kV/in

@Thickness 0.125 in
Processing Properties Metric English Comments
Melt Temperature 190 - 274 °C
374 - 525 °F
Mold Temperature 38.0 - 82.0 °C
100 - 180 °F