Inno-Comp INNOPOL® CS 1-3120 B DEL 20% Talc Filled Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 1-3120 B DEL 20% Talc Filled Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 1-3120 B DEL is developed for producing injection molded automotive components.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc @Temperature 23.0 °C |
0.0376 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | Normal; ISO 294 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | ISO 294 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Ash | 19 % @Temperature 600 °C |
19 % @Temperature 1110 °F |
ISO 3451-1/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 23 % | 23 % | ISO 527-1,-2 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.46 GPa | 357 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 2.73 GPa | 396 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 1.80 J/cm² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 4.60 J/cm² @Temperature 23.0 °C |
21.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.150 J/cm² @Temperature -30.0 °C |
0.714 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 162 °C | 324 °F | DSC; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
FMVSS 302 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive Materials | Pass | FMVSS 302 |
| Color | Black |
Users viewing this material also viewed the following:
- NeXolve Clear Optionox® Polyimide Film/Coating
- Parker Chomerics CHO-FORM® 5515 Robotically Dispensed Gasketing
- Garlock 5500 Compressed Inorganic Fiber Gasketing, Nitrile Binder
- Universal Wire Works 19-9WMo (AMS 5782) Filler Metal
- ChevronTexaco Meropa® 220
- ExxonMobil MEK Methyl Ethyl Ketone
- Chosun Refractories BPSC-95 Gas Purging Refractory
- Abatron AboCast/AboCure 8501-6/8501-4 High Temperature Resistant Epoxy
- H.C. Starck Amperit® 588.088 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr) 53/20 µm
Copyright © lookpolymers.com All Rights Reserved