Inno-Comp INNOPOL® CS 2-3130 NU UV-Stabilized 30% Talc-Filled Polypropylene Block-Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler
Manufacturer Inno-Comp Ltd
Trade Name INNOPOL® CS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Inno-Comp INNOPOL® CS 2-3130 NU UV-Stabilized 30% Talc-Filled Polypropylene Block-Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
INNOPOL® CS 2-3130 NU is an UV-stabilized 30% talc-filled polypropylene block-copolymer compound /PP-B TD30 (ISO 1043)/.INNOPOL® CS 2-3130 NU is recommended for producing injection molded products where the required property is high strength and high stiffness besides low shrinkage and low-temperature resistance.All information provided by INNO-COMP.
Physical Properties Metric English Comments
Density 1.13 g/cc

@Temperature 23.0 °C
 0.0408 lb/in³

@Temperature 73.4 °F
 ISO 1183
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 28.0 MPa
4060 psi
50 mm/min; ISO 527-1,-2
Elongation at Yield 2.7 %
2.7 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 3.10 GPa
450 ksi
1 mm/min; ISO 527-1,-2
Flexural Modulus 3.20 GPa
464 ksi
2 mm/min; ISO 178
Charpy Impact, Notched 0.260 J/cm²

@Temperature -20.0 °C
 1.24 ft-lb/in²

@Temperature -4.00 °F
 ISO 179/1eA
0.450 J/cm²

@Temperature 23.0 °C
 2.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 129 °C
264 °F
ISO 75-1,-2
Descriptive Properties Value Comments
Color Natural