Ipiranga Petrochem PH 0950 Polypropylene

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Ipiranga Petrochem
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ipiranga Petrochem PH 0950 Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not produce catalyst residues (due to its high catalytic yield).Raw materials are supplied by COPESUL. Following pre-treatment, they are sent, with the catalytic system, into two loop reactors and one gas-phase reactor. This plant produces PP homopolymer, random copolymer, heterophase copolymer and terpolymer.The product leaves the reactors in the shape of spherical grains. The grains are sent to the extrusion site, where stabilizers are added to them. They are then turned into pellets by an extruding press. The pelletized material is first sent to mixing and storage silos. Later, this material is sent to the packaging area.Applications:wrappers for sweets and candies
Physical Properties Metric English Comments
Melt Flow 7.0 - 9.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
7.0 - 9.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238-00
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D785-98
Tensile Strength, Yield 38.0 MPa
5510 psi
ASTM D638-02
Elongation at Yield 7.1 %
7.1 %
ASTM D638-02
Flexural Modulus 1.61 GPa
234 ksi
1% secant; ASTM D790-02
Izod Impact, Notched 0.400 J/cm
0.749 ft-lb/in
ASTM D256-03
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 113 °C
235 °F
ASTM D648-97
Vicat Softening Point 155 °C
311 °F
ASTM D1525-97
Optical Properties Metric English Comments
Haze 81 %

@Thickness 2.30 mm
81 %

@Thickness 0.0906 in
ASTM D1003A-00