Jackon JACKOCELL® R311 Expanded Polystyrene Packaging and Shape Molding
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Expanded Polystyrene (EPS) |
| Manufacturer | Jackon GmbH |
| Trade Name | JACKOCELL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Jackon JACKOCELL® R311 Expanded Polystyrene Packaging and Shape Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
100% Polystyrene.Pre-expansionHigh density stability in pre-expansion, transportation and silo storage reduces opportunity losses through achieving typical lower average density during regular production. It is the unique design of polystyrene chains that gives the high strength advantages to Jackocell® R311 in pre-expansionShape MouldingFast molding cycles, good fusion, and easy to reach good surface. The additional broad moulding window further reduces waste material and maintains a high quality to the extent that it can be recognized long term on productivity and financial earnings.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0140 g/cc | 0.000506 lb/in³ | 1.2 minute residence time pre-expander |
| 0.0170 g/cc | 0.000614 lb/in³ | 2.4 minute residence time pre-expander | |
| 0.0200 g/cc | 0.000723 lb/in³ | 0.9 minute residence time pre-expander | |
| 0.0280 g/cc | 0.00101 lb/in³ | 0.5 minute residence time pre-expander | |
| Water Absorption | 4.6 % | 4.6 % | 13-20 hour silo ageing time; Volume% |
| Bead Size | 0.700 - 1.00 mm | 0.0276 - 0.0394 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 0.333 MPa | 48.3 psi | 16 hour silo aging time, 20 kg/m^3 |
| 0.340 MPa | 49.3 psi | 32 hour silo aging time, 20 kg/m^3 | |
| 0.346 MPa | 50.2 psi | 48 hour silo aging time, 20 kg/m^3 | |
| 0.352 MPa | 51.1 psi | 64 hours silo aging time, 20 kg/m^3 | |
| Compressive Strength | 0.120 MPa | 17.4 psi | 16 hour silo aging time, 20 kg/m^3 |
| 0.124 MPa | 17.9 psi | 32 hour silo aging time, 20 kg/m^3 | |
| 0.127 MPa | 18.5 psi | 48 hour silo aging time, 20 kg/m^3 | |
| 1.32 MPa | 191 psi | 64 hours silo aging time, 20 kg/m^3 |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Blowing Agent Content | >= 6.0 % | >= 6.0 % | Pentane |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Coefficient of Variation (%), max | 15 | |
| Moulding Cycle Time (sec) | 100 | 64 hours silo aging time, 20 kg/m^3 |
| 110 | 48 hour silo aging time, 20 kg/m^3 | |
| 140 | 32 hour silo aging time, 20 kg/m^3 | |
| 210 | 6 hour silo aging time, 20 kg/m^3 |
Users viewing this material also viewed the following: